Synthesis and characterization of LiCoO 2-coated LiNi 0.8Co 0.15Al 0.05O 2 cathode materials

WanMin Liu,Guorong Hu,Ke Du,Zhongdong Peng,Yanbing Cao,Qiang Liu

DOI: https://doi.org/10.1016/j.matlet.2012.05.100

IF: 3

2012-01-01

Materials Letters

Abstract:An electrochemically active LiCoO2 layer was coated onto the surface of LiNi0.8Co0.15Al0.05O2 by a molten salt method. The 3.0wt.% LiCoO2-coated LiNi0.8Co0.15Al0.05O2 exhibited excellent electrochemical performance, with an initial discharge capacity of 196.2mAh·g−1 and capacity retention of 98.7% after 50cycles when cycled at 0.2C rate between 2.8 and 4.3V. Moreover, the cycle performance and rate capability of the coated sample were better than that of the bare one. Electrochemical impedance spectroscopy measurements showed that the decrease of NiO-type surface layer on the coated sample is the major reason for the improvement of electrochemical performance of LiCoO2-coated LiNi0.8Co0.15Al0.05O2 cathode.