Abstract:A simple ultrasonic method was developed to synthesize rod-like SnS nanocrystals, using tin chloride and thioacetamide as starting materials, ethanolamine and water as solvents. The as-obtained nanostructures were characterized by X-ray diffraction (XRD) study, energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and Ultraviolet-visible spectrophotometry (UV). From the XRD pattern, the reflection peaks of the as-obtained samples can be indexed to the orthorhombic structure with lattice constants a = 3.99, b = 4.34, c = 11.20 angstrom, which are very consistent with the values in the standard card of SnS phase (JCPDS No. 39-0354). No characteristic peak was observed for other impurities such as SnO2 and SnS2, implying the formation of single-phase tin monosulfide. The quantification calculation shows the ratio of Sn/S to be 51.30/48.70 via the EDS analysis. These data clearly indicate that the as-prepared rod-like nanostructures are exactly SnS. TEM results show that, the SnS nanorods have length about 100nm and width less than 30nm. The direct and indirect band gaps of the SnS nanorods are determined to be 1.53 eV and 1.34 eV, respectively. The band gaps of the as-obtained SnS nanorods showed blue shifts due to the quantum size effects. The ultrasonic condition is believed to be critical for the formation of SnS with pure phase. For it provides the energy to form rod-like nanostructures and helps preventing the hydrolysis of Sn2+ to form tin oxides and hydrates. Also, it prevents oxidation of the final products.

Simple Route for Synthesis of Tin Dioxide Nanorods Based on Improved Solid State Reactions

Synthesis and characterization of SnO2 nanorods

A Simple Route to Synthesize Multiform Structures of Tin Oxide Nanobelts and Optical Properties Investigation

Sub-2 Nm SnO2 Nanocrystals: A Reduction/oxidation Chemical Reaction Synthesis and Optical Properties

Large-scale synthesis of rutile SnO2 nanorods

Facile Synthesis of Single-Crystal Tin Oxide Nanorods with Tunable Dimensions Via Hydrothermal Process

Synthesis and optical properties of SnO2 nanorods

Synthesis and Characterization of Rutile SnO2 Nanorods

Novel Route to WO<i><sub>x</sub></i>Nanorods and WS<sub>2</sub>Nanotubes from WS<sub>2</sub>Inorganic Fullerenes

A new route to self-assembled tin dioxide nanospheres: fabrication and characterization.

A Simple and Effective Route for the Synthesis of Crystalline Silver Nanorods and Nanowires

A simple and novel route for the preparation of ZnO nanorods

Ultrasonically Assisted Synthesis of Tin Sulfide Nanorods at Room Temperature

Synthesis of Sno2 Nanoribbons by Direct Oxidation of Tin Powders

Facile and Surfactant-Free Route to Nanocrystalline Mesoporous Tin Oxide

Synthesis of SnO 2 @sns 2 Core–shell Nanorods by Double Crucible Method and Their Photocatalysis

Preparation of SnO2 nanorods by annealing SnO2 powder in NaCl flux

A Novel Hydrothermal Route to Synthesize Solid SnO 2 Nanospheres and Their Photoluminescence Property

Novel Synthesis of Tin Dioxide Nanoribbons Via A Mild Solution Approach

Controllable Synthesis of Single-Crystal SnO2nanowires and Tri-Crystal SnO2nanobelts

A Novel and Low-Temperature Hydrothermal Synthesis of SnO 2 Nanorods