Abstract:Polydimethylsiloxane (PDMS) is usually used to obtain favorable performances of waterborne polyurethane (WPU) such as higher hardness, exceptional thermal stability and lower interfacial tension. However, there is always a problem that waterborne polyurethane (WPU) often performs weak tensile strength, lower tenacity and brittle property at room temperature when polydimethylsiloxane (PDMS) is embedded into the backbone of polyurethane. The study aims to address the problem by constructing dual crosslinking structure, namely introducing trimethylolpropane as an intramolecular crosslinking agent into prepolymers and then adding waterborne polycarbodiimide (SK-400) as a post-crosslinking agent in order to further enlarge the degree of crosslinking and mainly make up for the shortcoming that mechanical property decreases when polydimethylsiloxane (PDMS) was inserted into molecule chains. Initially a novel inner-crosslinking prepolymer (SiWPU) comprising polydimethylsiloxane need to be synthesized successfully by inserting trimethylolpropane into prepolymers. Then the sample SiWPU-3 was picked out as a matrix resin and dropwise added polycarbodiimide (SK-400) as a post-crosslinking agent into the matrix resin (C–SiWPU). As pH was gradually lowering following the evaporation of triethylamine in the emulsion (C–SiWPU), carboxyl groups (COOH) in prepolymers started to react with SK-400 (NCN) to form twofold crosslinking structure. When 0%, 2%, 4%, 6%, and 8 wt% of waterborne polycarbodiimide (SK-400) was incorporated into the solution, the tensile strengths are 47.8 MPa, 57.7 MPa, 65 MPa, 57.6 MPa and 54.5 MPa and the elongation at break 732%, 756%, 798%, 707% and 700%. The crosslinking density of SiWPU-3 without the addition of waterborne polycarbodiimide (SK-400) is 3.86 × 10−3 mol/cm3. As 6 wt% of waterborne polycarbodiimide (SK-400) was added into the emulsion of SiWPU-3, the crosslinking density of C–SiWPU-6 (6 wt% SK-400) is 6.19 × 10−3 mol/cm3. The films show excellent extensibility and exceptional tenacity. Hence, the emulsion is able to be applied in leather industry.

Effects of HDI/IPDI Ratio on Properties of Waterborne Polyurethane

Preparation and properties study of waterborne polyurethane synthesized by mixing polyester diols and isocyanates

Synthesis and Characterization of Eugenol‐based Silicone Modified Waterborne Polyurethane with Excellent Properties

Distribution of Hydrophilic Monomer Units and Its Effect on the Property of the Water Dispersion of Polyurethaneurea Anionomer

Effect of Sepiolite-Loaded Fe<sub>2</sub>O<sub>3</sub> on Flame Retardancy of Waterborne Polyurethane

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Synthesis and modification of waterborne polyurethane derived from hybrid CO2-based polyols

Effects of Isosorbide on the Microphase Separation and Properties of Waterborne Polyurethane Coatings

Effect of Water Content on the Aggregation and Adhesion Properties of Waterborne Polyurethane

Synthesis and characterization of waterborne polyurethane emulsions based on poly(butylene itaconate) ester

Characterization of an Aqueous Dispersion of a Hydrophilic Polyisocyanate for Waterborne Two-Pack Polyurethane Coatings

Preparation and properties of polyester diol and waterborne polyurethane

Effects of aminopropyl-terminated polydimethylsiloxane on structure and properties of waterborne polyurethane-acrylate

Improving water resistance of waterborne polyurethane coating with high transparency and good mechanical properties

Design, Preparation and Properties of Polyurethane Dispersions via Prepolymer Method

Preparation and Properties of Two-Component and Double-Crosslinking Waterborne Polyurethane-Acrylic Dispersions

Synthesis of waterborne polyurethane by inserting polydimethylsiloxane and constructing dual crosslinking for obtaining the superior performance of waterborne coatings

Preparation, Characterization, and Property Analysis of Environmentally Friendly Waterborne Polyurethane-Acrylate

Synthesis and Characterization of Nonionic Waterborne Polyurethane and Application to Wool Fabric Finishing

Synthesis and application of comb-like waterborne polyurethane as a dispersant for disperse dyes

Effects of Isocyanate Structure on the Properties of Polyurethane: Synthesis, Performance, and Self-Healing Characteristics