Abstract:We reported a low-temperature solution-processed method for the fabrication of AlOx thin films in the memory device. The detailed study is carried out to figure out the effect of varying annealing temperatures (150, 200, 250, 300, and 350 degrees C) on resistive switching characteristics of solution-processed aluminum oxide dielectric. The dielectric properties of AlOx films under different annealing temperatures were evaluated by atomic force microscopy (AFM), thermogravimetric analysis-differential scanning calorimetry (TGA-DSC), X-ray diffraction (XRD), attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR) and X-ray photoelectron spectroscopy (XPS) firstly. Then the AlOx films were used as the switching dielectric layer for a variety of low-temperature solution-processed oxide resistive random access memory (RRAM) devices. It was found that forming voltage increased with increasing annealing temperature and forming free behavior could be achieved by 200 degrees C sample. No repeatable resistance switching characteristics were observed in the devices with minimum (150 degrees C) and maximum (350 degrees C) annealing temperatures. Compared with the ALD-derived AlOx based RRAM devices in previous study, enhanced performance like small forming voltage, large resistance ratio (<180) and narrow resistance and voltage distribution was achieved by the solution-processed AlOx based ones at the optimized low annealing temperatures of 200 to 250 degrees C, which would be applied in the bionic circuit simulated by synapses and neural networks. All three samples (200, 250, and 300 degrees C) obtained switching endurance up to 300 cycles and data retention over 10(4) s. Furthermore, the solution based fabrication method also has the potential in the flexible memory application due to the merit of the low-temperature process.

Effect of Annealing Temperature on Resistance Switching Behavior of Mg0.2Zn0.8O Thin Films Deposited on ITO Glass

Annealing effect on electrical properties of high-k MgZnO film on silicon

Annealing effects of In2O3 thin films on electrical properties and application in thin film transistors

Effects of Post-Annealing Treatment on the Structural and Optical Properties of Cubic Mg Chi Zn1-Chi O Thin Films Grown on Sapphire

Effects of Annealing Conditions on Resistive Switching Characteristics of SnOx Thin Films

Dependence of Annealing Temperatures on the Optimized Resistive Switching Behavior from Siox (X=1.3) Films

Influence of Annealing Temperature on the Properties of Transparent Conductive and Near-Infrared Reflective Zno : Ga Films

Improvements in Resistive and Capacitive Switching Behaviors in Ga2O3 Memristors via High-Temperature Annealing Process

Effect of Annealing Temperature on Electrical Properties of ZTO Thin-Film Transistors

Effects of thermal annealing on the electrical characteristics of In-Ga-Zn-O thin-film transistors with Al2O3 gate dielectric

Enhanced Resistive Switching Performance of Aluminum Oxide Dielectric with a Low Temperature Solution-Processed Method

Effect of annealing on optical properties of Mg(x)Zn(1-x)Othin films deposited at low temperature

[Effects of Annealing Temperature on the Structure and Optical Properties of ZnMgO Films Prepared by Atom Layer Deposition].

Effect of Thermal Annealing on the Properties of Transparent Conductive In–Ga–Zn Oxide Thin Films

Effect of Annealing Temperature on the Electrical Properties of ZnO Thin-Film Transistors

Resistance switching study of stoichiometric ZrO2 films for non-volatile memory application

Improved Resistance Switching Stability in Fe-Doped ZnO Thin Films Through Pulsed Magnetic Field Annealing

Effect of Post-Annealing Treatments on the Properties of Zn1−xCdxO Films on Glass Substrates

The Effect of Annealing Temperature on the Optical and Electrical Properties of Cubic MgZnO Films Grown by RF Magnetron Sputtering

Temperature Dependence of Resistive Switching Behaviors in Resistive Random Access Memory Based on Graphene Oxide Film.

Effects Of High-Temperature Thermal Annealing On The Electronic Properties Of In-Ga-Zn Oxide Thin Films