On the Interface and Mechanical Property of Ti/Al–6%Cu–0.5%Mg–0.4%Ag Bimetal Composite Produced by Cold-Roll Bonding and Subsequent Annealing Treatment

Jiangtao Peng,Zhiyi Liu,Peng Xia,Mao Lin,Sumin Zeng

DOI: https://doi.org/10.1016/j.matlet.2012.01.052

IF: 3

2012-01-01

Materials Letters

Abstract:Ti/Al–6%Cu–0.5%Mg–0.4%Ag bimetallic composite has been successfully produced by cold-roll bonding and subsequent annealing treatment. The threshold deformation is about 44% total rolling reduction in a single rolling pass. The highest interlaminer shear strength up to about 40MPa in the composite is obtained by 515°C/12h annealing treatment. The calculation indicates that the tensile strength of Ti/Al–6%Cu–0.5%Mg–0.4%Ag bimetal composite is consistent with the mixture rule obeyed by composites. TiAl3 is the first and the only phase formed during the annealing process, and it experiences a lateral growth in the direction parallel to the interface then a thickening in the direction perpendicular to the interface.