Synthesis, Structure and Luminescence Properties of Mn-doped MgAl2O4 Red-Emitting Phosphors with Varying Sintering Temperature
Jiahao Zha,Chongjun He,Fangzhou Chen,Hongwei Wang,Biao Dong,Lijuan Liu,Mingjun Xia,Chenguang Deng,Qian Li,Yuangang Lu,Huiting Chen
DOI: https://doi.org/10.1007/s10895-024-03937-w
2024-09-27
Journal of Fluorescence
Abstract:Oxide matrix red-emitting phosphors are deemed as excellent color converters for white light emitting diodes (WLEDs) and laser diodes (LDs). Manganese-doped MgAl 2 O 4 powder was synthesized by a solid-state reaction method at different sintering temperatures. Microstructure shows that grain size is mainly in the range of 0.2–5 μm, and grain agglomeration occurs with increased sintering temperature. XPS analysis indicates that the doped Mn ion exhibits a valence state of + 4 within the MgAl 2 O 4 matrix. The diffraction peak of the phosphors is shifted by the sintering temperature, which affects lattice constant. Upon excitation by 300 nm ultraviolet light, the samples emit asymmetric broadband red light within the range of 620–720 nm, attributed to Mn 4+ ion's transition from 2 E g to 4 A 2g states. With the increasing temperature, the main emission peak shifts from 677 nm to 650 nm, ascribed to the change in energy level ( 2 E g ) resulting from the reduction of Al 2 O 3 phase. Crystal field theory confirmed that Mn 4+ ions are within a strong crystal field environment created by MgAl 2 O 4 matrix. By affecting particle size and crystallinity, the sintering temperature influences the fluorescence lifetime of the Mn 4+ ion. Notably, these red-emitting phosphors exhibits remarkable thermal stability as their emission intensity remains approximately at 58% of initial intensity even at elevated temperature (435 K). Consequently, Mn 4+ : MgAl 2 O 4 red-emitting phosphors with high thermal stability render them promising candidates for WLED applications.
chemistry, physical, analytical,biochemical research methods