Abstract:Al-doped ZnSn(OH)6 crystalline precursors (Zn1-xAlxSn(OH)6+x) were synthesized with 4 wt% triethanolamine (TEOA). After dehydration of the precursors at high temperature (HT), the resulting Zn1-xAlxSnO3+x/2 (denoted as ZAxSO) samples with amorphous structure were obtained. The phase structure transition can be significantly distinguished by their XRD patterns. The pristine ZnSnO3 sample composed of microscale particles shows an excellent ultraviolet absorption from 200 to 400 nm, and Al-doping makes its UV absorption weakened in the wavelength of 300–400 nm. However, nano-TiO2 decoration enables the UV absorption strengthened in the wavelength range. Less content of Al-doping (x≤0.15) can improve the ethanol sensitivity of ZnSnO3 sample at HT (>200 °C). When x is 0.1, the resulting ZA0.1SO sample is more sensitive to 500 ppm ethanol than other samples, with a response value of 336.0 at 260 °C. After decoration of 10 wt% nano-TiO2, the operating temperature of the ZA0.1SO sample under 385 nm UV illumination is greatly decreased from 260 to 110 °C, with a high ethanol response of 231.4 at the same concentration. The effects of Al-doping and nano-TiO2 decoration on the gas-sensing properties of the pristine ZnSnO3 sample were discussed based on the structure analysis and UV absorption of the sensitive materials.

UV-illumination room-temperature gas sensing activity of carbon-doped ZnO microspheres

Enhanced performance of the tangerines-like CuO-based gas sensor using ZnO nanowire arrays

Broad-spectrum UV absorption and gas-sensing improvement of ZnSnO3 cubic particles based on Al-doping and nano-TiO2 decoration

Broad-spectrum UV absorption and gas-sensing improvement of ZnSnO<sub>3</sub> cubic particles based on Al-doping and nano-TiO<sub>2 </sub>decoration

High Performance Gas Sensor Based on ZnO/CuO Heterostructures

Morphology, photoluminescence and gas sensing of Ce-doped ZnO microspheres

Carbon Nanotube-ZnO Nanosphere Heterostructures: Low-Temperature Chemical Reaction Synthesis, Photoluminescence, and Their Application for Room Temperature NH 3 Gas Sensor

From ZnO nanorods to 3D hollow microhemispheres: solvothermal synthesis, photoluminescence and gas sensor properties

Synthesis of flower-like Al doped ZnO microstructures by hydrothermal process and analysis of their gas sensing properties

Enhancing gas-sensing property and sensing mechanism at molecule level of the hollow microspheres assembled with ZnO nanoflakes exposing {001} facets

Adsorption Behaviors of Gas Molecules on the Surface of ZnO Nanocrystals under UV Irradiation

Preparation of transparent amorphous ZnSnO3 cubic nanoparticles and light-induced homostructures: Application in UV sensor and room-temperature gas sensor

UV-enhanced Oxygen Sensing with Tunable ZnO Nanorod Arrays at Room Temperature

Morphology Modulation of ZnO Microspheres and Improvement of Triethylamine Detection Performance by Introducing Carbon Dots

Realizing room-temperature self-powered ethanol sensing of ZnO nanowire arrays by combining their piezoelectric, photoelectric and gas sensing characteristics

Room-temperature methane sensors based on ZnO with different exposed facets: A combined experimental and first-principle study

Preparation of tungsten-doped zinc oxide thin films by co-sputtering for micro-gas sensing devices

UV-activated Room Temperature Single-Sheet ZnO Gas Sensor

Enhanced ethanol sensing performance of N-doped ZnO derived from ZIF-8

Investigation of gas sensitivity of Sb-doped ZnO nanoparticles

Hydrothermal Preparation and Gas Sensing Properties of Zn-doped SnO2 Hierarchical Architectures