Broad-spectrum UV absorption and gas-sensing improvement of ZnSnO3 cubic particles based on Al-doping and nano-TiO2 decoration

Xiuyu Wang,Tao Tao,Zhinan Qi,Binxin Leng,Wen Xu,Jiajun Ma,Mingming Wang

DOI: https://doi.org/10.1016/j.snb.2020.129013

2021-01-01

Abstract:<p>Al-doped ZnSn(OH)₆ crystalline precursors (Zn_1-<em>_x</em>Al<em>_x</em>Sn(OH)₆₊<em>_x</em>) were synthesized with 4 wt% triethanolamine (TEOA). After dehydration of the precursors at high temperature (HT), the resulting Zn_1-<em>_x</em>Al<em>_x</em>SnO₃₊<em>_x</em>_/2 (denoted as ZA<em>_x</em>SO) samples with amorphous structure were obtained. The phase structure transition can be significantly distinguished by their XRD patterns. The pristine ZnSnO₃ sample composed of microscale particles shows an excellent ultraviolet absorption from 200 to 400 nm, and Al-doping makes its UV absorption weakened in the wavelength of 300–400 nm. However, nano-TiO₂ decoration enables the UV absorption strengthened in the wavelength range. Less content of Al-doping (<em>x</em>≤0.15) can improve the ethanol sensitivity of ZnSnO₃ sample at HT (&gt;200 °C). When <em>x</em> is 0.1, the resulting ZA_0.1SO sample is more sensitive to 500 ppm ethanol than other samples, with a response value of 336.0 at 260 °C. After decoration of 10 wt% nano-TiO₂, the operating temperature of the ZA_0.1SO sample under 385 nm UV illumination is greatly decreased from 260 to 110 °C, with a high ethanol response of 231.4 at the same concentration. The effects of Al-doping and nano-TiO₂ decoration on the gas-sensing properties of the pristine ZnSnO₃ sample were discussed based on the structure analysis and UV absorption of the sensitive materials.</p>

chemistry, analytical,electrochemistry,instruments & instrumentation