Highly sensitive ethanol gas sensor based on CuO/ZnSnO3 heterojunction composites

Shouwen Yu,Xiaohua Jia,Jin Yang,Sizhe Wang,Yong Li,Haojie Song

DOI: https://doi.org/10.1016/j.matlet.2021.129531

IF: 3

2021-05-01

Materials Letters

Abstract:<p>Monitoring ethanol is importance to our life. Here, CuO/ZnSnO₃ hollow microspheres were synthesized through in-situ precipitation method. CuO/ZnSnO₃ was characterized by XRD, XPS, SEM and TEM. The characterization results showed that CuO/ZnSnO₃ hollow microsphere with a radius of 0.8-1.4 μm. The sensing performances of the as-prepared nanocomposites were examined and compared with ZnSnO₃ and CuO. Gas sensing results revealed that the 8% CuO/ZnSnO₃ sensor exhibits excellent ethanol response (R_a/R_g=131-100 ppm), which was 3-3.5 times higher than that of ZnSnO₃ and CuO at the optimal operating temperature (160 ℃), respectively. The simple production process and superior gas response make CuO/ZnSnO₃ applicable to more occasions where ethanol exists. The improved performance can be attributed to the p-n heterojunction between CuO and ZnSnO₃.</p>

materials science, multidisciplinary,physics, applied

What problem does this paper attempt to address?

This paper aims to solve the problems of how to improve the sensitivity of ethanol gas sensors and reduce the working temperature. Specifically, the researchers attempt to improve the performance of ZnSnO₃ - based gas sensors by constructing CuO/ZnSnO₃ heterojunction composite materials.

### Background and problems of the paper

1. **Importance of ethanol detection**:
- As a common volatile organic gas (VOC), ethanol has wide applications in fields such as national defense chemical industry, medical and health, and food industry.
- Therefore, monitoring and controlling the ethanol concentration in the air is crucial for ensuring people's quality of life.

2. **Limitations of existing ZnSnO₃ sensors**:
- ZnSnO₃ is an important n - type metal oxide semiconductor (MOS). Because it is easy to prepare, has low cost and is environmentally friendly, it is used as a sensing material for detecting various VOC gases.
- However, ZnSnO₃ - based gas sensors have some drawbacks, such as low sensitivity and high working temperature.

3. **Improvement methods**:
- Constructing heterojunctions is one of the effective methods to improve the gas - sensing performance of ZnSnO₃. For example, Bai et al. prepared NiO₂/ZnSnO₃ composite materials and found that its sensitivity to formaldehyde was enhanced; Umar et al. reported that CuO nanoplates showed a high response to ethanol.

### Research objectives of the paper

To overcome the above problems, this paper synthesized CuO/ZnSnO₃ hollow microspheres by in - situ precipitation method and tested their gas - sensing properties. The research shows that the response value of the 8% CuO/ZnSnO₃ sensor to 100 ppm ethanol reached 131, which is much higher than the response values of pure ZnSnO₃ and CuO (3 - 3.5 times of them respectively). In addition, the working temperature of this sensor is 160 °C, which is significantly lower than the optimal working temperature of pure ZnSnO₃ (220 °C).

### Main contributions

1. **High sensitivity**: The CuO/ZnSnO₃ composite material shows a high response to ethanol (R_a/R_g = 131), which is 3 - 3.5 times higher than that of pure ZnSnO₃ and CuO.
2. **Low working temperature**: The optimal working temperature is reduced from 220 °C to 160 °C.
3. **Fast response and recovery time**: The response time is 13 seconds and the recovery time is 8 seconds.
4. **Good stability and repeatability**: After a long - term stability test of 49 days, the sensor still maintains a high response.

In conclusion, this research successfully improved the sensitivity of ethanol gas sensors and reduced the working temperature by constructing CuO/ZnSnO₃ heterojunction composite materials, showing its broad application prospects in daily ethanol gas monitoring.