Abstract:To assess the life of a new diesel aluminium alloy piston under thermal shock loads, thermo-mechanical fatigue (TMF) testing was conducted to characterise the TMF properties of the piston alloy, and an empirical model based on the constraint ratio concept was proposed to predict the TMF life of the piston. Considering that the empirical model required expensive experimental support, a platform with high-frequency induction heating was established to simulate the force on the piston under thermal shock loads to calculate the piston life using the thermal shock test. Additionally, a finite element method was developed to compute the distributions of temperature, strain, and stress during this process. The characteristics of crack initiation and propagation in TMF test rods and piston mock-ups were also investigated. The results showed that the TMF test rod suffered brittle fracture with brittle quasi-cleavage features. The microcracks mainly occurred in primary Si particles due to stress concentration around the primary Si particles induced by the difference between the thermal expansion coefficients of Si and Al. From a macro perspective, the piston initially cracked at the rim above the pinhole, where the stress is larger than that along other directions. From a micro perspective, the protrusions of various sizes on the piston rim were induced by the compression stresses at high temperature. The piston cracks usually initiate around primary Si particles, propagate along the edge of primary Si in a straight line, bifurcate and then stop at a certain depth. If the piston was only heated, cracks or plastic deformations were not produced. The piston life can be assessed using the proposed empirical model based on the constraint ratio concept or thermal shock testing based on the developed platform. The difference between the predicted and experimental life was not greater than 7%.

Metallographic study of laser thermal fatigue damage on piston

Study on Mechanism of Laser Thermal Damage on Piston

INTEGRATED TECHNOLOGY FOR DETECTION AND REPAIR OF MECHANICAL COMPONENT SURFACE FATIGUE MICROCRACKS USING PULSED LASER

Experiment and numerical simulation study of thermal fatigue of an aluminum alloy piston

Thermal fatigue crack growth behavior of ZCuAl10Fe3Mn2 alloy strengthened by laser shock processing

On the Microstructure, Residual Stress and Fatigue Performance of Laser Metal Deposited TC17 Alloy Subjected to Laser Shock Peening

Experimental and Computational Study on Thermo‐mechanical Fatigue Life of Aluminium Alloy Piston

Experimental and Numerical Studies of Fatigue Behavior of Ti6Al4V Alloy Treated by Laser Shock Peening

Effects of laser shock processing, solid solution and aging, and cryogenic treatments on microstructure and thermal fatigue performance of ZCuAl10Fe3Mn2 alloy

Effect of laser shock peening on the high-temperature fatigue performance of 7075 aluminum alloy

A Study of Fatigue Damage Evolution on Pulsed Nd:Yag Ti6al4v Laser Welded Joints

On the Use of Infrared Thermography for Analysis of Fatigue Damage in Ti6Al4V-Welded Joints

Experimental study on improving high-cycle fatigue performance of TC11 titanium alloy by laser shock peening

Effects of Laser Shock Peening on Microstructure and Fatigue Behavior of Ti–6Al–4V Alloy Fabricated Via Electron Beam Melting

High Cycle Fatigue Performance in Laser Shock Peened TC4 Titanium Alloys Subjected to Foreign Object Damage

Microstructure and Mechanical Properties of Laser Metal Deposited AlSi10Mg Alloys

Microstructure and residual stress modulation of 7075 aluminum alloy for improving fatigue performance by laser shock peening

Failure analysis of the piston used in a pneumatic down the hole impactor

Regain the Fatigue Strength of Laser Additive Manufactured Ti Alloy Via Laser Shock Peening

Evaluation of Plastic Deformation and Prediction of Thermal Mechanical Fatigue Life of an Al–Si Alloy Piston for Diesel Engines

Effect Study and Application to Improve High Cycle Fatigue Resistance of TC11 Titanium Alloy by Laser Shock Peening with Multiple Impacts