Abstract:This paper presents the experimental methods and findings in obtaining the strain behavior of mortar during freezing and thawing cycles (FTC) at the meso-scale under fully saturated condition and the coefficient of thermal expansion (CTE) and elastic modulus of mortar after FTC tests. A heat-cool cycle test comparing an oven-dried and undried mortar was also performed prior to the FTC test, confirming that oven drying at 105 degrees C does not affect the CTE of samples, thereby ensuring the reliability of the results. During FTC with constant moisture content, a limitation in the increase in tensile strain was observed and this tensile strain decreased until contraction was observed. The contraction is attributed to the removal of gel pore water arising from negative pressures. Due primarily to the absence of available water supply, the displaced pore water cannot be refilled, which results in contraction at the end of the FTC. More importantly, the results show that after FTC, the CTE of frost damaged mortar increases while its elastic modulus decreases, primarily owing to microcracking when frost damage sets in. Microcracks act as broken bridges that can detach the aggregate from the hardened cement paste and in effect reduces the thermal restraints that each part (fine aggregate and cement paste) exerts on the other. The hardened cement paste can then expand/contract more freely under temperature variation, and thus can significantly affect (increase) the CTE of the whole composite (mortar). Further, stress transfer in the material is prevented due to microcracking resulting in elastic modulus reduction.

Effect of porosity on thermal expansion coefficient of cement pastes and mortars

Change of the Coefficient of Thermal Expansion of Mortar Due to Damage by Freeze Thaw Cycles

Determining Porosity and Pore Network Connectivity of Cement-Based Materials by a Modified Non-Contact Electrical Resistivity Measurement: Experiment and Theory

Empirical Estimation of Pore Size Distribution in Cement, Mortar, and Concrete

The effects of high temperature heating on the gas permeability and porosity of a cementitious material

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

Temperature Dependence of Thermal Diffusivity of OPC and CAC Cement Paste

Analysis of Pore Structure, Contact Angle and Pore Entrapment of Blended Cement Pastes from Mercury Porosimetry Data

Towards Better Characterizing Thermal Conductivity of Cement-Based Materials: the Effects of Interfacial Thermal Resistance and Inclusion Size

Influence of Porosity on Compressive and Tensile Strength of Cement Mortar

Evaluating the chloride diffusion coefficient of cement mortars based on the tortuosity of pore structurally-designed cement pastes

Effects of water and temperature variations on deformation of limestone aggregates, cement paste, mortar and High Performance Concrete (HPC)

Molecular dynamics study of the effect of moisture and porosity on thermal conductivity of tobermorite 14 Å

Factors Influencing the Capillary Water Absorption Characteristics of Concrete and Their Relationship to Pore Structure

Pore structure characterization of cement paste by different experimental methods and its influence on permeability evaluation

Effect of Curing Conditions on Pore Structure of Cement Based Materials

Effect of Pore Shape on the Thermal Conductivity of Partially Saturated Cement-Based Porous Composites

A New Analytical Method to Predict Permeability Properties of Cementitious Mortars: the Impacts of Pore Structure Evolutions and Relative Humidity Variations

Distribution of porosity surrounding a microfiber in cement paste

Both Plasticizing and Air-Entraining Effect on Cement-Based Material Porosity and Durability

A Study on the Relationship Between Porosity of the Cement Paste with Mineral Additives and Compressive Strength of Mortar Based on This Paste