Experimental investigation of polypyrrole coating doped with chromium nitride nanoparticles on aluminum alloy bipolar plates for PEMFC
S. J. Narasimharaju,K. Annamalai,B. Poorna Chandra Rao,P. Sakthivel
DOI: https://doi.org/10.1007/s10853-024-10467-0
IF: 4.5
2024-11-28
Journal of Materials Science
Abstract:Proton exchange membrane fuel cells (PEMFCs) are efficient, environmentally friendly devices for applications such as transportation and stationary power generation. The bipolar plate (BP) is a key component in PEMFCs, responsible for electrical conductivity, gas distribution, and water management. 6061 aluminum alloy (AA) is commonly used for BPs due to its lightweight and conductive properties, but it is prone to corrosion. This study examines the efficacy of polypyrrole (PPy) coatings that are enhanced with chromium nitride (CrN) nanoparticles (NPs) on 6061 AA specimens. These coatings greatly enhance the corrosion resistance, polarization resistance, and protection efficiency of the 6061 AA. Out of all the coatings that were tested, the PPy-CrN 0.2 coating stood out as the top performer. It showed a positive corrosion potential ( E corr ) of − 0.51 V versus SCE and a significantly lower corrosion current ( I corr ) of 0.44 μA/cm 2 . This coating demonstrates the highest polarization resistance value of 47,904.53 Ω/cm 2 and achieves an impressive protection efficiency of 72.84%, surpassing other coated specimens. In addition, the PPy-CrN 0.2 coating demonstrates exceptional protective properties, boasting an impressive impedance value ( Z ) of 5019 Ω/cm 2 . This underscores its remarkable effectiveness in preventing the infiltration of corrosive ions, as confirmed by electrochemical impedance spectroscopy. Future characterization studies, including X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), and scanning electron microscopy/energy-dispersive spectroscopy (SEM/EDS) will further elucidate the structural and functional properties of the PPy-CrN 0.2 coating. Additionally, interfacial contact resistance (ICR) measurements were conducted to assess the electrical performance of the coating. The PPy-CrN 0.2 coating demonstrated the lowest ICR value of 18.4 mΩ/cm 2 at a compaction pressure of 1.4 MPa, confirming its improved conductivity and suitability for PEMFC applications. These findings highlight the importance of ICR testing in evaluating the overall performance and efficiency of the PPy-CrN 0.2 coating in PEMFC systems.
materials science, multidisciplinary