Abstract:The relevant phase transformations induced by atomic diffusion at the vicinity of Nb/TiAl heterogenous interface were systematically investigated by establishing a novel system of TiAl-Nb couple via metallurgical bonding of Nb block and γ-TiAl powders by hot pressing sintering and post-annealing treatments. As a result, the resultant diffusion layer, acting as adhesive region linking the Nb and TiAl substrates, thickened with the increase of annealing temperature and the prolongation of holding time, which could be well described by the developed power function. A series of intermediate phases initially nucleated at the Nb/TiAl interface and grew toward both substrates, which was the result of the exchange, partitioning and recombination of solute atoms in the light of vacancy-mediated substitutional diffusion pattern. The phase transformation path on the Nb side was β→η→η + σ→σ→β 0 →β 0 + γ n , while that on the TiAl side was γ→γ ss →γ ss + α→(γ + α)+ (α + β 0 )→α + β 0 →β 0 + γ n . Then the disorder-order transition of α→α 2 and β 0 →B2 occurred during cooling. The progress of phase transformation slowed down as the diffusion proceeded, which was attributed to the decrease in atomic substitution efficiency due to the reduction of atomic concentration gradient and the extension of migration distance. In such a case, the banded σ ba split into spike σ sp along the direction of maximum concentration gradient, and then shrunk to isolated σ is until completely dissolved in β 0 regime, principally dominated by Ti occupying Nb sublattices. The lenticular γ n existed mainly in the form of twins, resulting from the lattice reconstruction in accordance with the orientation relationship of 111γ//110β0 and 1̅10γ//11̅1β0 in the Al partitioning region during the spontaneous fluctuation of atomic concentration of β 0 regime. These findings filled some fundamental gaps with respect to TiAl-Nb diffusion reaction system, and afforded profound insights into the development of high-performance TiAl/Nb composites with tailorable microstructure.

Ternary Interdiffusion Coefficients in Α2-Phase Ti3Al/Nb System

Effect of Substrate Characteristics on Interdiffusion Coefficients of Ni and Al Atoms in Β-Nial Phase of Aluminide Coatings

Diffusion mobilities for the B2-b.c.c. phase in the Ni–Al binary system

Assessment of Mobilities of the B2 Phase in the Nickel-Chromium-Aluminum System

Atomic diffusion and microstructural evolution at the Nb/TiAl heterogenous interfaces during annealing at elevated temperatures

The Reaction Process of NbAl Interface in Rod-in-Tube Strands

Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

Investigation of the ordering and atomic site occupancies of Nb-doped TiAl/Ti3Al intermetallics

Diffusion in titanium and titanium—niobium alloys

Interdiffusion Coefficients and Strengthening Effects of Nb, Ta, and Zr in the α2-Ti3Al Phase

Interdiffusion and Atomic Mobility in BCC-A2 Mo-Zr and Mo-Nb-Zr Alloys with Very Steep Composition Profiles

Thermodynamic aspects of oxidation for Nb alloying gamma-TiAl intermetallic compounds

Composition and temperature dependence of α2 phase decomposition in high Nb-containing lamellar γ-TiAl alloys: Experiments and first-principles calculations

Orderly Nucleation and Competitive Growth Behaviors of Ti-Al Intermetallic Compounds in Ti/TiAl3 Diffusion Couple under High Temperature

First-principles thermodynamic investigation on the α phases in TiO and TiNb binary system

Investigation on diffusion kinetics of Ti-X binary systems at 1300-1500°C

Ternary diffusion in the α and γ phases of the Fe-Ni-P system

Experimental study on phase relations in the Al-Mo-Nb ternary system

THERMODYNAMIC ASPECTS OF OXIDATION FOR Nb ALLOYING γ-TiAl INTERMETALLIC COMPOUNDS

Effect of Nb and B on the Precipitation Behaviors in Al-Ti-Nb Balanced Ratio Ni-Based Superalloy: A Phase-Field Study

The Effect of Nb Doping on the Properties of Ti-Al Intermetallic Compounds Using First-Principles Calculations