Hydrothermal Synthesis and Fluorescence Properties of Cerium Phosphate Nanomaterials with Different Crystal Structures

Li-Ge YANG,Bo ZHOU,Tian-Hong LU,Chen-Xin CAI

DOI: https://doi.org/10.3969/j.issn.1000-0518.2008.06.017

2007-01-01

Abstract:CePO4 fluorescence nanomaterials with different crystal structures and morphology was hydrothermally synthesized and characterized with the techniques of X-ray diffraction(XRD),transmission electron microscopy(TEM),scanning electron microscopy(SEM) and fluorescence spectroscopy,etc.The effects of pH and temperature on the crystal structure,morphology and fluorescent intensity of CePO4 were investigated.The SEM results indicated that CePO4 prepared in acidic solution(pH=1,120 ℃) were nanorods,while CePO4 prepared in alkaline solution(pH=12,120 ℃) were nanoparticles.The XRD results showed that CePO4 prepared in acidic(pH=1,120 ℃) solution had a hexagonal crystal structure.However,the crystallinity of CePO4 obtained in the acidic solution was better than that of CePO4 obtained in the alkaline solution.The crystal structure of CePO4 depended on the preparation temperature.The CePO4 had a hexagonal crystal structure when it was prepared at 120 ℃ and pH=1.CePO4 with monoclinic and hexagonal crystal structures can be simultaneously formed with increasing the preparation temperature.Only CePO4 with the monoclinic structure was obtained when the temperature was 200 ℃.Fluorescence spectra indicated that both hexagonal and monoclinic CePO4 showed a broad emission band at between 300~400 nm due to the 5d-4f emission of cerium.However,the fluorescence intensity of the monoclinic CePO4 was stronger than that of hexagonal one.