Abstract:CePO4 fluorescence nanomaterials with different crystal structures and morphology was hydrothermally synthesized and characterized with the techniques of X-ray diffraction(XRD),transmission electron microscopy(TEM),scanning electron microscopy(SEM) and fluorescence spectroscopy,etc.The effects of pH and temperature on the crystal structure,morphology and fluorescent intensity of CePO4 were investigated.The SEM results indicated that CePO4 prepared in acidic solution(pH=1,120 ℃) were nanorods,while CePO4 prepared in alkaline solution(pH=12,120 ℃) were nanoparticles.The XRD results showed that CePO4 prepared in acidic(pH=1,120 ℃) solution had a hexagonal crystal structure.However,the crystallinity of CePO4 obtained in the acidic solution was better than that of CePO4 obtained in the alkaline solution.The crystal structure of CePO4 depended on the preparation temperature.The CePO4 had a hexagonal crystal structure when it was prepared at 120 ℃ and pH=1.CePO4 with monoclinic and hexagonal crystal structures can be simultaneously formed with increasing the preparation temperature.Only CePO4 with the monoclinic structure was obtained when the temperature was 200 ℃.Fluorescence spectra indicated that both hexagonal and monoclinic CePO4 showed a broad emission band at between 300~400 nm due to the 5d-4f emission of cerium.However,the fluorescence intensity of the monoclinic CePO4 was stronger than that of hexagonal one.

Synthesis and characterization of mixed-morphology CePO4 nanoparticles

Redox Hydrothermal Synthesis of Cerium Phosphate Microspheres with Different Architectures

Controlled Syntheses and Photoluminescence Characterization of Monoclinic Cerium Orthophosphate with Nanostructure

Hydrothermal Synthesis and Fluorescence Properties of Cerium Phosphate Nanomaterials with Different Crystal Structures

Phase evolution and photoluminescence enhancement of CePO 4 nanowires from a low phosphate concentration system

SYNTHESIS AND CHARACTERIZATION OF Dy3+-DOPED HEXAGONAL ONE-DIMENSIONAL CERIUM PHOSPHATE NANOMATERIAL POWDERS

Hydrothermal growth and morphology evolution of CePO4 aggregates by a complexing method

Synthesis of stable cerium oxide nanoparticles coated with phosphonic acid-based functional polymers

Biological reduction-deposition and luminescent properties of nanostructured CePO4@NaCe(SO4)2(H2O) and CePO4

Synthesis and luminescence of CePO<sub>4</sub> and CePO<sub>4</sub>:Tb hollow and core–shell microspheres composed of single-crystal nanorods

Morphology-selective synthesis method of nanopolyhedra and square-like CeO 2 nanoparticles

Synthesis and characterization of ceria nanoparticles by complex-precipitation route

Morphology-Control Synthesis and Photoluminescence Characterization of Cerium Compounds in Phosphoric Acid System

Synthesis of CePO4 nano-wires with improved photoluminescent properties by co-crystallizing with nano-sized CeO2.

Synthesis, spectroscopic and luminescent properties of nanosized powders of yttrium phosphates doped with Er3+ ions

Synthesis and Enzymatic Activity of Ni , Ru Co-doped CePO4 Nanomaterials

Synthesis, Structure and Optical Properties of Cerium(Iii) Triphosphate Cep3o9

Facile Sonochemical Synthesis of CePO4:Tb/LaPO4core/shell Nanorods with Highly Improved Photoluminescent Properties

SYNTHESIS AND PHOTOCHEMICAL PROPERTIES OF MICACEOUS CERIUM PHOSPHATES

Synthesis and Properties of Cerium Oxide Nanoparticles

Synthesis and Characterization of Plate-Like Cerium Phosphate Via Soft Solution Processing