Abstract:A series of samples, prepared from mechanical mixtures of inorganic salts (MoO3, CuCl2, NiCl26H2O, and Ni(NO3)26H2O) with zeolites (NaZSM-5, NaY, NaY, and MCM-41), have been investigated by X-ray diffraction (XRD), differential thermal analysis (DTA), the adsorption of probing molecules, and the determination of pore size distribution. After the heating of MoO3with zeolites at 723 K for 24 h, the samples (MoO3/NaZSM-5/NaY/MCM-41=0–0.088/0–0.24/0–0.45 g/g) show only those X-ray peaks assigned to zeolites, the characteristic peaks of MoO3having disappeared completely, which suggests that MoO3is highly dispersed in the pores of zeolites. Similar phenomena are observed for the samples of CuCl2/NaZSM-5, CuCl2/NaY, NiCl2/NaZSM-5, NiCl26H2O/NaY, and Ni(NO3)26H2O/NaY. In contrast, the inorganic salts of NiCl26H2O and Ni(NO3)26H2O cannot be dispersed into the channels of NaZSM-5 zeolite due to the limitation of the channel size. These results suggest that the dispersion only occurs under the condition that the diameter of the inorganic salts is less or similar to the pore size of the zeolites. Also, we observed that the dispersion capacity of the inorganic salts is strongly related to the pore size of the zeolites. Furthermore, the isotherms for probing molecules show that the dispersion of inorganic salts into zeolites leads to significant change in the pore size of zeolites. The MoO3/NaY samples exhibit that the pore size was selectively formed at 6.8–8.0, 6.0–6.8, 4.3–6.0, and 3.0–4.3 Å with MoO3loading at 0.08, 0.16, 0.21, and 0.24 g/g, respectively. Therefore, it is proposed that we could modify the pore sizes of zeolites to various degrees, which may be very useful to design suitable pores of zeolites for the catalysts in catalytic reactions. Catalytic data in selective reduction of NO by propylene at the temperature of 300°C show that CuCl2/HZSM-5 catalyst prepared from the dispersion method exhibits much higher catalytic conversion (39%: N2yield) than that (21%: N2yield) of CuZSM-5 catalyst prepared from the ion-exchange method.

New Route for Dispersion of Inorganic Salts Onto the Channel Surfaces of Microporous Crystals: High Dispersion of CuCl2 in Zeolites Using a Microwave Technique

The High Dispersion of CuCl 2 in NaZSM-5 by Using Microwave Technique

The High Dispersion of CuCl2in ZSM-5 by Using Microwave Method

Dispersion of Inorganic Salts into Zeolites and Their Pore Modification

Studies of the interaction between CuCl and HY zeolite for preparing heterogeneous CuI catalyst

Probing The Porosity Of Cocrystallized Mcm-49/Zsm-35 Zeolites By Hyperpolarized Xe-129 Nmr

Investigation of the Microporous Structure and Non-Framework Aluminum Distribution in Dealuminated Nanosized HZSM-5 Zeolite by 129xe NMR Spectroscopy

Probing the Porosity of Cocrystallized MCM-49/ZSM-35 Zeolites by Hyperpolarized 129xe NMR.

Zeolites modified by CuCl for separating CO from gas mixtures containing CO 2

Control of crystallization rate and morphology of zeolite silicalite-1 in solvent-free synthesis

Synthesis and characterization of MCM-49/ZSM-35 composite zeolites in the hexamethyleneimine and cyclohexamine system

High efficiency CO adsorbent CuCl/zeolite

Preparation of CuNaY Zeolites with Microwave Irradiation and Their Application for Removing Thiophene from Model Fuel

Dispersion Capacities of KCl and NaCl in Zeolites

Methodsfor Dispersing MoO3 on Zeolite Molecular Sieve ZSM-5

Preparation of new porous materials Al2O3/NaY by microwave radiation

Microwave synthesis conditions dependent catalytic performance of hydrothermally aged CuII-SSZ-13 for NH3-SCR of NO

Calcination Of Kaolinite And Synthesis Of 4a Zeolite Used In Detergent With Microwave Method

Ammonium removal from aqueous solutions using microwave-treated natural Chinese zeolite

Studies on the Dispersion States of Nickel Salt and Oxide on NaY Zeolites

Synthesis of highly active Cu(I)-Y(III)-Y zeolite and its selective adsorption desulfurization performance in presence of xylene isomers