Abstract:The pyrolyzed carbon supported ferrum polypyrrole (Fe-N/C) catalysts are synthesized with or without selected dopants, p-toluenesulfonic acid (TsOH), by a facile thermal annealing approach at desired temperature for optimizing their activity for the oxygen reduction reaction (ORR) in O2-saturated 0.1 mol/L KOH solution. The electrochemical techniques such as cyclic voltammetry (CV) and rotating disk electrode (RDE) are employed with the Koutecky-Levich theory to quantitatively obtain the ORR kinetic constants and the reaction mechanisms. It is found that catalysts doped with TsOH show significantly improved ORR activity relative to the TsOH-free one. The average electron transfer numbers for the catalyzed ORR are determined to be 3.899 and 3.098, respectively, for the catalysts with and without TsOH-doping. The heat-treatment is found to be a necessary step for catalyst activity improvement, and the catalyst pyrolyzed at 600 °C gives the best ORR activity. An onset potential and the potential at the current density of – 1.5 mA/cm2 for TsOH-doped catalyst after pyrolysis are 30 mV and 170 mV, which are more positive than those without pyrolized. Furthermore, the catalyst doped with TsOH shows higher tolerance to methanol compared with commercial Pt/C catalyst in 0.1 mol/L KOH. To understand this TsOH doping and pyrolyzed effect, X-ray diffraction (XRD), scanning electron microscope (SEM) and X-ray photoelectron spectroscopy (XPS) are used to characterize these catalysts in terms of their structure and composition. XPS results indicate that the pyrrolic-N groups are the most active sites, a finding that is supported by the correspondence between changes in pyridinic-N content and ORR activity that occur with changing temperature. Sulfur species are also structurally bound to carbon in the forms of C–Sn–C, an additional beneficial factor for the ORR.

Effects of Heat Treatment on the Structure, Morphology and Electrocatalytic Activity of Cobalt Hydroxide Electrocatalyst

Effects of hydrothermal treatment on the catalytic activity of cobalt-doped catalysts for oxygen reduction reaction

Effect of Heat Treatment Temperature on the Pt3Co Binary Metal Catalysts for Oxygen Reduced Reaction and DFT Calculations

Development of High-Performance Cathode Catalyst of Polypyrrole Modified Carbon Supported CoOOH for Direct Borohydride Fuel Cell

Atomic Structure of Polypyrrole-Modified Carbon-Supported Cobalt Catalyst

Synergy among transition element, nitrogen, and carbon for oxygen reduction reaction in alkaline medium

Synchrotron Radiation in Situ X-ray Absorption Fine Structure and in Situ X-ray Diffraction Analysis of a High-Performance Cobalt Catalyst Towards the Oxygen Reduction Reaction

Effect of Heat Treatment on the Structure and Functional Characteristics of the PtCo/C Catalyst

Heat treatment-induced Co3+ enrichment in CoFePBA to enhance OER electrocatalytic performance

Influences of Carbon Support on the Electrocatalysis of Polypyrrole-Modified Cobalt Hydroxide in the Direct Borohydride Fuel Cell

Oxygen reduction reaction on a polypyrrole-modified, carbon-supported cobalt hydroxide catalyst

In Situ Study of the Catalytic Mechanism for the Oxygen Reduction Reaction on a Polypyrrole Modified Carbon Supported Cobalt Hydroxide Cathode in Direct Borohydride Fuel Cells.

Oxygen Electroreduction on Heat-Treated Multi-Walled Carbon Nanotubes Supported Iron Polyphthalocyanine in Acid Media

A Non-Noble Material Cathode Catalyst Dual-Doped with Sulfur and Nitrogen As Efficient Electrocatalysts for Oxygen Reduction Reaction

Effects of heat-treatment temperature on microstructure and electrochemical properties of AB5 type MlNi 3.60Co 0.85Mn 0.40Al 0.15 hydride electrode alloy

Synthesis and effect of electrode heat-treatment on the superior lithium storage performance of Co 3 O 4 nanoparticles

Effect of Pyrolysis Conditions on the Performance of Co–Doped MOF–Derived Carbon Catalysts for Oxygen Reduction Reaction

A cobalt porphyrin-bridged covalent triazine polymer-derived electrode for efficient hydrogen production

Highly Active Electrocatalysts for Oxygen Reduction from Carbon-Supported Copper-Phthalocyanine Synthesized by High Temperature Treatment

Synthesis of Dual-Doped Non-Precious Metal Electrocatalysts and Their Electrocatalytic Activity for Oxygen Reduction Reaction

Evidence of carbon-supported porphyrins pyrolyzed for the oxygen reduction reaction keeping integrity