Abstract:The pyrolyzed carbon supported ferrum polypyrrole (Fe-N/C) catalysts are synthesized with or without selected dopants, p-toluenesulfonic acid (TsOH), by a facile thermal annealing approach at desired temperature for optimizing their activity for the oxygen reduction reaction (ORR) in O2-saturated 0.1 mol/L KOH solution. The electrochemical techniques such as cyclic voltammetry (CV) and rotating disk electrode (RDE) are employed with the Koutecky-Levich theory to quantitatively obtain the ORR kinetic constants and the reaction mechanisms. It is found that catalysts doped with TsOH show significantly improved ORR activity relative to the TsOH-free one. The average electron transfer numbers for the catalyzed ORR are determined to be 3.899 and 3.098, respectively, for the catalysts with and without TsOH-doping. The heat-treatment is found to be a necessary step for catalyst activity improvement, and the catalyst pyrolyzed at 600 °C gives the best ORR activity. An onset potential and the potential at the current density of – 1.5 mA/cm2 for TsOH-doped catalyst after pyrolysis are 30 mV and 170 mV, which are more positive than those without pyrolized. Furthermore, the catalyst doped with TsOH shows higher tolerance to methanol compared with commercial Pt/C catalyst in 0.1 mol/L KOH. To understand this TsOH doping and pyrolyzed effect, X-ray diffraction (XRD), scanning electron microscope (SEM) and X-ray photoelectron spectroscopy (XPS) are used to characterize these catalysts in terms of their structure and composition. XPS results indicate that the pyrrolic-N groups are the most active sites, a finding that is supported by the correspondence between changes in pyridinic-N content and ORR activity that occur with changing temperature. Sulfur species are also structurally bound to carbon in the forms of C–Sn–C, an additional beneficial factor for the ORR.

Synergy among transition element, nitrogen, and carbon for oxygen reduction reaction in alkaline medium

Synergistic Interactions Between Co Nanoparticles and Unsaturated Co-N2 Sites for Efficient Electrocatalysis

Highly Active Cofe Alloy Nanoparticlesencapsulated in N-Doped Carbon Nanostructures for Oxygen Reduction Reaction in Both Alkaline and Acidic Media

(Digital Presentation) The Optimization of Polypyrrole Concentration to Synthesize Hollow Fe, Co, and Nitrogen Doped Carbon Spheres with Improved Oxygen Reduction Reaction Performance

Oxygen reduction reaction on a polypyrrole-modified, carbon-supported cobalt hydroxide catalyst

Metal (metal = Fe, Co), N codoped nanoporous carbon for efficient electrochemical oxygen reduction

Hybrids Based on Transition Metal Phosphide (mn2p, Co2P, Ni2P) Nanoparticles and Heteroatom-Doped Carbon Nanotubes for Efficient Oxygen Reduction Reaction

A novel strategy for realizing high nitrogen doping in Fe3C-embedded nitrogen and phosphorus-co-doped porous carbon nanowires: efficient oxygen reduction reaction catalysis in acidic electrolytes

Pyrolyzed Co-Nx/C Electrocatalysts Supported on Different Carbon Materials for Oxygen Reduction Reaction in Neutral Solution

Synergistic coupling of P-doped Pd4S nanoparticles with P/S-co-doped reduced graphene oxide for enhanced alkaline oxygen reduction

Novel nanowire-structured polypyrrole-cobalt composite as efficient catalyst for oxygen reduction reaction

Bimetallic ZnCo zeolitic imidazolate framework/polypyrrole-polyaniline derived Co/N-doped carbon for oxygen reduction reaction

Nitrogen and Carbon Co-Doped CoO x Nanostructures for Oxygen Reduction

Nitrogen and Carbon Co-Doped CoOx Nanostructures for Oxygen Reduction

Synergistically Enhanced Oxygen Reduction Electrocatalysis by Atomically Dispersed and Nanoscaled Co Species in Three-Dimensional Mesoporous Co, N-codoped Carbon Nanosheets Network

Effects of pyrrole polymerizing oxidant on the properties of pyrolysed carbon-supported cobalt-polypyrrole as electrocatalysts for oxygen reduction reaction

Preparation and Electrochemical Characteristics of MnOx–CoTMPP∕BP Composite Catalyst for Oxygen Reduction Reaction in Alkaline Solution

CoO/Co/N-C nanoparticles embedded in carbon as mediate for oxygen reduction electrocatalysts

Tuning Cobalt and Nitrogen Co-Doped Carbon to Maximize Catalytic Sites on a Superabsorbent Resin for Efficient Oxygen Reduction

Secondary doping of Mn/Co bimetallic ZIF-derived catalysts for the oxygen reduction reaction

Synthesis of Dual-Doped Non-Precious Metal Electrocatalysts and Their Electrocatalytic Activity for Oxygen Reduction Reaction