Abstract:Electrocatalysts consisting of polypyrrole (PPY) and Co deposited on carbon black (CB) at several compositions were prepared and tested for the oxygen reduction reaction (ORR) in a HClO4 buffer (pH=1) using a rotating ring-disk electrode (RRDE). It was determined that the most favorable catalyst composition (prior to calcination) had a CB:PPY weight ratio of 2 and a pyrrole:Co (i.e., PY:Co) molar ratio of 4. This catalyst had an onset potential of 0.785V (vs. RHE) and a mass activity of ca. 1A/gcata at the fuel cell relevant voltage of 0.65V. Furthermore, it was found that the number of electrons exchanged during the ORR with the catalyst was ca. 3.5 and resulted in 28% yield of H2O2 at 0.65V, which hints to an indirect 4e− reduction of O2 to H2O, with H2O2 as an intermediate. From energy dispersive spectroscopy (EDS) and extended X-ray absorption fine structure (EXAFS) analysis, it is proposed that a PY:Co ratio of 4 favors the formation, prior to calcination, in the catalyst precursor of Co–N complexes in which Co is coordinated to 3 or 4 N atoms, resulting in strong Co–N interactions that limit the formation upon calcination of low ORR activity Co nanoparticles. These Co–N complexes give rise upon calcination to CoNx−2 sites in which the coordination of Co could favor the adsorption on them of O2, which would make those sites particularly active and selective. At the same mass activity of 1A/gcata, the voltage yielded by the catalyst was 200mV lower than that for a state-of-the-art Pt (10wt.%) catalyst, whose H2O2 output at 0.85V was 39% and involves the exchange of 3.2e−, overall making our material an attractive substitute to noble metal ORR electrocatalysts.

Development of High-Performance Cathode Catalyst of Polypyrrole Modified Carbon Supported CoOOH for Direct Borohydride Fuel Cell

Coral-like cobaltous sulfide/N,S-codoped carbon with hierarchical pores as highly efficient noble metal-free electrocatalyst for oxygen reduction reactions

High-Loading Cobalt Oxide Coupled with Nitrogen-Doped Graphene for Oxygen Reduction in Anion-Exchange-Membrane Alkaline Fuel Cells

In Situ Study of the Catalytic Mechanism for the Oxygen Reduction Reaction on a Polypyrrole Modified Carbon Supported Cobalt Hydroxide Cathode in Direct Borohydride Fuel Cells.

FeS As a Promising Cathode Catalyst for Direct Borohydride Fuel Cells

Noble-metal-free Co-N-c Catalyst Derived from Cellulose-Based Poly(ionic Liquid)s for Highly Efficient Oxygen Reduction Reaction.

Vacancy-assisted Oxygen Reduction Reaction on Cobalt-Based Catalysts in Direct Borohydride Fuel Cell Revealed by In-Situ XAFS and XRD

Oxygen reduction reaction on a polypyrrole-modified, carbon-supported cobalt hydroxide catalyst

Influences of Carbon Support on the Electrocatalysis of Polypyrrole-Modified Cobalt Hydroxide in the Direct Borohydride Fuel Cell

A cobalt-pyrrole coordination compound as high performance cathode catalyst for direct borohydride fuel cells

Polypyrrole regulates Active Sites in Co‐based Catalyst in Direct Borohydride Fuel Cells

Development of the Cathode Catalyst for Direct Borohydride Fuel Cell

Cobalt–polypyrrole–carbon black (Co–PPY–CB) electrocatalysts for the oxygen reduction reaction (ORR) in fuel cells: Composition and kinetic activity

A cobalt polypyrrole composite catalyzed cathode for the direct borohydride fuel cell

Performance Degradation of A Direct Borohydride Fuel Cell

Functionalization of Polyvinyl Alcohol Composite Membrane by CoOOH for Direct Borohydride Fuel Cells

Electrocatalysts for the Anodic Oxidation of Borohydrides

Prevention of Active-Site Destruction During the Synthesis of High Performance Non-Pt Cathode Catalyst for Fuel Cells

Introducing Catalyst in Alkaline Membrane for Improved Performance Direct Borohydride Fuel Cells

CoO nanorods/C as a high performance cathode catalyst in direct borohydride fuel cell

A highly efficient axial coordinated CoN5 electrocatalyst via pyrolysis-free strategy for alkaline polymer electrolyte fuel cells