EFFECT OF Si CONTENT ON ORDERING DEGREE AND ELECTROMAGNETIC CHARACTERISTICS IN FeSiAl ALLOYS

T.D. Zhou,L.J. Deng,D.F. Liang

DOI: https://doi.org/10.1016/s1006-7191(08)60038-1

2008-01-01

Abstract:FeSiAl alloys ribbons synthesized by melt-quench were annealed in vacuum at 873 K for 60 min.The flaky powders were prepared by milling the annealed ribbons for 70 h.After milling,the powders were heat treated at 573 K for 90 min.The order- ing degree of the powders lattice structure was analyzed by X-ray diffraction （XRD）. The measurement of specific saturation magnetization was carried out by vibrating samples magnetometer （VSM）.Complex permittivity and complex permeability in the frequency band of 0.5-18 GHz were measured with the vector network analyzer.The ordering degree of the superlattice structure increased from 0.27 to 0.49.Complex permittivity and complex permeability decreased with increasing Si content.After or- dering,the specific saturation magnetization decreased from 134.2 to 85.0 A·m~2·kg -1 . For use in anti-EMI material,the total contents of Si and Al in FeSiAl alloys should be controlled at a low level.