Abstract:Tungsten (W) has been selected as the divertor material in ITER based on its promising thermal and mechanical properties. Despite these advantages, continued investigation has revealed W to undergo extreme surface morphology evolution in response to relevant fusion operating conditions. These complications spur the need for further exploration of W and other innovative plasma facing components (PFCs) for future fusion devices. Recent literature has shown that alloying of W with other refractory metals, such as tantalum (Ta), results in the enhancement of key PFC properties including, but not limited to, ductility, hydrogen isotope retention, and helium ion (He+) radiation tolerance. In the present study, pure W and W–Ta alloys are exposed to simultaneous and sequential low energy, He+ and deuterium (D+) ion beam irradiations at high (1223 K) and low (523 K) temperatures. The goal of this study is to cultivate a complete understanding of the synergistic effects induced by dual and sequential ion irradiation on W and W–Ta alloy surface morphology evolution. For the dual ion beam experiments, W and W–Ta samples were subjected to four different He+: D+ ion ratios (100% He+, 60% D+ + 40% He+, 90% D+ + 10% He+ and 100% D+) having a total constant He+ fluence of 6 × 1024 ion m−2. The W and W–Ta samples both exhibit the expected damaged surfaces under the 100% He+ irradiation, but as the ratio of D+/He+ ions increases there is a clear suppression of the surface morphology at high temperatures. This observation is supported by the sequential experiments, which show a similar suppression of surface morphology when W and W–Ta samples are first exposed to low energy He+ irradiation and then exposed to subsequent low energy D+ irradiation at high temperatures. Interestingly, this morphology suppression is not observed at low temperatures, implying there is a D–W interaction mechanism which is dependent on temperature that is driving the suppression of the microstructure evolution in both the pure W and W–Ta alloys. Minor irradiation tolerance enhancement in the performance of the W–Ta samples is also observed.

Effect of Deuterium Ion Implantation on Microstructures of Fe- M ( M =V, W, Ta) Alloys

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

TEM Studies of 1 MeV Fe+ Ion-Irradiated W Alloys by Wet Chemical Method: High-Temperature Annealing and Deuterium Retention

Properties of Potassium Doped and Tantalum Containing Tungsten after Heavy Ion Irradiation

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Microstructure Evolution and Effect on Deuterium Retention in TiC- and ZrC-Doped Tungsten under He+ Ion Irradiation

Effects of Tantalum Concentration on the Microstructures and Mechanical Properties of Tungsten-Tantalum Alloys

Microstructural Evolution of CLAM Steel under 3.5 MeV Fe 13+ Ion Irradiation

Microstructure Evolution and Effect on Deuterium Retention in Oxide Dispersion Strengthened Tungsten During He+ Irradiation

Deuterium retention in W and binary W alloys irradiated with high energy Fe ions

The effect of W2+ irradiation and He+ exposure on W-Ta alloy fabricated via SPS

Influences of displacement damage due to heavy ion irradiation on deuterium retention in CLF-1 steel

Irradiation hardening and deuterium retention behaviour of tungsten under synergistic irradiations of 3.5 MeV Fe 13+ ions and deuterium plasma

Suppression of surface microstructure evolution in W and W–Ta alloys during simultaneous and sequential He and D ion irradiation in fusion relevant conditions

Effect of helium and its synergism with displacement damage on microstructure of CLAM steel investigated by single, sequential and simultaneous Fe and He ion irradiations

Microstructure and deuterium retention after ion irradiation of W–Lu2O3 composites

Irradiation effects on binary tungsten alloys at elevated temperatures: Vacancy cluster formation, precipitation of alloying elements and irradiation hardening

Effect of annealing on the microstructure behavior of D+-irradiated W-2vol.%TiC composite prepared by wet-chemical method

Helium ions irradiation of tantalum-zirconium carbide thin films: The effect of acetylene gas contents

Influence of annealing and keV-ion implantation into tungsten on deuterium retention and permeation: The dependence on bulk and surface microstructure

Correlation Between Deuterium Retention and Microstructure Change for Tungsten under Triple Ion Implantation