Oxidation Behavior and Kinetics of SiC/alumina–borosilicate Coating for Carbon–carbon Composites

Jun Li,Ruiying Luo,Yaping Chen,Qiao Xiang,Chen Lin,Peng Ding,Na An,Jiwei Cheng

DOI: https://doi.org/10.1016/j.apsusc.2008.06.169

IF: 6.7

2008-01-01

Applied Surface Science

Abstract:A SiC/alumina–borosilicate double-layer coating was prepared by a two-step slurry technique for the protection of carbon–carbon composites from oxidation. SEM, XRD and EDX analysis showed that the inner layer coating obtained from the first step consisted of β-SiC, Si and SiO2. The outer layer consisted of B4C, Al, amorphous SiO2 and quartz. The oxidation behavior and kinetics of the SiC/alumina–borosilicate coating were investigated. It was found that the as-prepared coating could effectively protect carbon–carbon composites from oxidation at 1300°C for 100h. The isothermally oxidation kinetics could be described by Microflaws Model and Diffusion Model. During short-time oxidation, the overall oxidation kinetics was determined by the transport processes through microflaws, which resulted in a linear growth law. While during oxidation of longer time, the weight loss rate was controlled by the diffusion processes in the coating with growing oxide layer, which led to a parabolic growth law.