Abstract:In the present work, effects of ZrC addition (10, 15, 20, 25 vol%) on microstructure and mechanical properties of ZTA20mol% (Zirconia-20mol% Toughened Alumina) ceramic composites were investigated. Samples were prepared by Hot Pressing Sintering (HP) at 1 600 ℃ and 30 MPa for a soaking time of 2 hours. Microstructures were characterized by XRD, Raman, SEM and TEM. XRD and Raman spectra results revealed that only ZrC, α-Al2O3 and ZrO2 were detected for all composites, indicating that these ceramic composites had excellent chemical compatibilities. SEM images showed refined microstructure was obtained, and the fracture surfaces exhibited a mixed process of transgranular and intergranular fracture. According to the TEM observations, some nano-sized ZrC particles dispersed inside Al2O3 grains and formed an intra/inter-type nanostructure. The relative densities and Vickers hardness were inversely proportional to ZrC content, which gradually decreased from 98.24% to 94.89%, from 1 847 to 1 691 HV1, respectively. Flexural strength and fracture toughness were tested by three-point bending method and single-edge notched beam method, respectively. The fracture toughness increased at first and then decreased with ZrC content increased from 0 to 25 vol%. The maximum value was 11.23 MPa.m1/2 with 20 vol% ZrC addition, with an enhancement of 51% compared to the undoped ZTA mixture. The flexural strength, with a maximum of 1 121 MPa without ZrC addition and decreased to 645MPa with ZrC-10(vol%) addition, then increased monotonously to 1084 MPa as the ZrC content increased from 10 to 25 vol%.

Preparation, microstructure and mechanical properties of ZrB2–ZrO2 ceramics

Microstructure and mechanical properties of ZrB2–SiC–ZrO2f ceramic

Microstructure and Mechanical Properties of ZrB2-SiC Composites

Microstructure and mechanical properties of hot pressed ZrC-SiC-ZrB 2 composites

Microstructure and Mechanical Properties of Zrb2-Based Composites Reinforced and Toughened by Zirconia

Microstructure and mechanical properties of zirconia-toughened ZrB2–MoSi2 composites prepared by hot-pressing

Microstructure and Mechanical Properties of Hot-Pressed ZrB2–SiC–ZrO2f Ceramics with Different Sintering Temperatures

Microstructure and Mechanical Properties of ZrO2-2 Mol% Y2O3 Ceramics

Comparison of ZrB 2-ZrO 2f ceramics prepared by hot pressing and pressureless sintering

Microstructure and Mechanical Properties of Zrb2-Based Ceramics

Effect of ZrO2 content on microstructure, mechanical properties and thermal shock resistance of (ZrB2+3Y-ZrO2)/BN composites

Effects of ZrB2 powders on microstructure and mechanical properties of ZrB2-SiCw ceramics

Microstructure and mechanical properties of ZrB2-based UHTC via reactive hot pressing

Microstructure and Mechanical Properties of Laminated ZrB2–SiC Ceramics with ZrO2 Interface Layers

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

Mechanical Properties of ZrO<sub>2</sub>–LaMgAl<sub>11</sub>O<sub>19</sub> Ceramics

Effect of ZrO 2 contents on the mechanical and thermal shock properties of ZrO 2p(3Y)/BN-SiO 2 ceramics composite

Microstructure and mechanical properties of hot pressed ZrB2–SiCp–ZrO2 composites

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Microstructure and Mechanical Properties of ZrB2–Nb Composite

The hybrid effect of SiC whisker coupled with ZrO 2 fiber on microstructure and mechanical properties of ZrB 2-based ceramics