Abstract:In this study, vinyl triethoxysilane (VTES), KH-560 and trimethylchlorosilane (TMCS) were used to modify the surface groups of commercially available nano-silica (SiO2, 50 nm), and ethylene vinyl acetate copolymer (EVA) was used as a film-forming agent. EVA/SiO2, EVA/V-SiO2, EVA/K-SiO2 and EVA/T-SiO2 coatings were prepared, respectively. The coatings were characterized by SEM, FTIR, TG and contact angle. It was found that when the mass percentage of SiO2 was 66 wt%, the hydrophobicity performance of the coating could be significantly improved by silica modification. Compared to the EVA/SiO2, the water contact angle (WCA) of the EVA/V-SiO2, EVA/K-SiO2 and EVA/T-SiO2 were increased by 24.0%, 14.4% and 24.6%, respectively. The FTIR results indicated that VTES, KH-560 and TMCS could effectively replace the -OH groups on the surface of the SiO2 after hydrolysis, resulting in the presence of water transport groups on the SiO2 surface. The TG results certified that TMCS had the highest substitution rate (24.6%) for the -OH groups on the SiO2 surface after the hydrolysis. Additionally, the SEM results indicated that T-SiO2 was more easily dispersed in the EVA film-forming agent, leading to a uniform micro–nano surface rough structure, which aligned with the Cassie–Wenzel model. The durability test had demonstrated that the EVA/T-SiO2 maintained its hydrophobic properties even after enduring 40,000 drops of water and the impact of 200 g of sand. Furthermore, it exhibited excellent resistance to acid corrosion, along with superior self-cleaning properties and an anti-fog performance. It also provided outstanding protection against high temperatures and UV radiation for outdoor applications.

Preparation of Durable Hydrophobic and Antireflective Silica Coating

Sol-gel Preparation of a Silica Antireflective Coating with Enhanced Hydrophobicity and Optical Stability in Vacuum

Hydrophobic and Optical Properties of Silica Antireflective Coating Prepared Via Sol-Gel Method

Preparation and Research of Hydrophobic PDMS/Nano-SiO2 Modified SiO2 Coating

Preparation and Properties of Methyl-Situ-modified Sol-Gel Hydrophobic Anti-Reflective SiO2 Coating

Preparation of Sponge-Like Porous SiO2antireflective Coatings with Excellent Environment-Resistance by an Acid-Catalysed Sol–gel Method

Hydrophobic and Optical Properties of HMDS/Silica Hybrid Antireflective Coating Prepared via Sol-gel Method

Preparation of Octyltrimethoxysilane Modified SiO$lt;inf$gt;2$lt;/inf$gt; Hydrophobic Antireflective Coating

Sol-Gel Preparation of HTMS-Silica Hydrophobic Coatings with High Environment-Resistance

Durable silica antireflective coating prepared by combined treatment of ammonia and KH570 vapor

A simple sol-gel method to prepare superhydrophilic silica coatings

Sol-gel Preparation of Hydrophobic Silica Antireflective Coatings with Low Refractive Index by Base/acid Two-Step Catalysis.

Study of the Preparation and Properties of Nano-structure Hydrophobic and Anti-reflective Silica Films

Preparation Of Silica Coatings With Continuously Adjustable Refractive Indices And Wettability Properties Via Sol-Gel Method

Design and Preparation of SiO2/TiO2/SiO2-TiO2 Antireflective Coatings with Excellent Abrasion-resistance and Transmittance Via Sol-Gel Process

The preparation and properties research of superhydrophobic organosilicone coating

Construction and performance of waterborne organosilicon anti-fouling coating based on hydrosilylation

A Simple Route to Prepare Hydrophobic, High Temperature Resistant and Antireflective Coatings

Superhydrophobic Coating Based on Nano-Silica Modification for Antifog Application of Partition Glass

Improving hydrophobic property of sol-gel antiveflective silica coatings by FAS

Sol−Gel Preparation of PDMS/Silica Hybrid Antireflective Coatings with Controlled Thickness and Durable Antireflective Performance