Strengthening mechanisms of a heterostructured pure aluminum with extraordinary mechanical properties
Junye Li,Guanghui Wang,Maofei Zhang,Jiahao Li,Xiaotian Fang,Xinkai Ma
DOI: https://doi.org/10.1016/j.matchar.2023.113049
IF: 4.537
2023-06-08
Materials Characterization
Abstract:To achieve superior mechanical properties in metallic materials, one promising way is to make them into heterogeneous structures (HS). In this work, a novel HS including grain size and dislocation density is developed in commercial pure aluminum through cold-rolling and subsequent partial annealing processes. Tensile tests show that the HS specimen, annealed at 150 °C for 2 min with ∼31.1% recrystallized grains, have a high yield strength of ∼121 MPa and a good uniform elongation of ∼8.5%. The yield strength increases by 10% and the ductility increases by 7 times compared with the as-rolled specimen, respectively. Detailed microstructure characterizations confirm that a significant strain gradient was generated near the interface between the hard zone and soft zone, in which the slip and plugging of geometrically necessary dislocations act as an important role in the abnormal hardening and strengthening phenomena of the HS specimen. To quantify the specific contribution of each strengthening mechanism, we compare the experimental measurements with the theoretical calculations and confirm that the multiple deformation modes are activated by the deformation stress. The hetero-deformation-induced hardening and strengthening effects are responsible for the superior mechanical properties of the heterostructured pure aluminum.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing