Abstract:Coarse grain and poor thermal stability of Mg17Al12 are usually present in the as-cast Mg–Al alloys, which are detrimental to the mechanical properties. In this work, the microstructure evolution, and mechanical properties of as-cast AZ31-1Y alloy with different cooling rates (4.0–29.9 °C/s) were systematically investigated by thermal analysis and microstructure characterization. The results show that the addition of Y to AZ31 alloy results in the formation of primary Al2Y and eutectic Al2Y, while suppressing the formation of β-Mg17Al12. The AZ31-1Y alloy with a cooling rate of 29.9 °C/s exhibits the finest grain, with a grain refinement efficiency 40.9 % higher than that of AZ31 alloy with a cooling rate of 4.0 °C/s. After heat treatment, the acicular eutectic Al2Y is modified into a granular shape and numerous nano-sized Al2Y precipitates are observed within the α-Mg matrix. The addition of Y can effectively improve the mechanical properties of AZ31 alloy under high cooling rates, but the mechanical properties deteriorate at slower cooling rates due to stress concentration caused by the agglomeration of large-sized Al2Y particles. The optimal mechanical properties of the AZ31-1Y alloy are achieved at a cooling rate of 29.9 °C/s combined with subsequent heat treatment, and its YS, UTS, and EL reached up to 69 MPa, 293 MPa, and 14.5 %, respectively. Moreover, the related strengthening mechanisms are quantified. It is believed that this work can provide guidance for controlling the microstructure and optimizing the mechanical properties of as-cast Mg–Al alloys.

Effect of Cooling Conditions on Grain Size of AZ91 Alloy

Effect of Grain Size on the Microstructure and Mechanical Properties of Mg-4Y-3Nd-0.5Zr Alloy

Effect of cooling rate on microstructure and mechanical properties of Mg-9Gd-4Y-1Zn-1Al alloy

The Effect of Cooling Rate on the Microstructure and Mechanical Properties of Mg–Zn–Gd-based Alloys

Effect of pouring temperature on thixotropic microstructure formation of AZ91

Effect of Cooling Rate on the Solidified Microstructure of Mg-Gd-Y-Zr Alloy

Effect of grain size distribution and texture on the cold extrusion behavior and mechanical properties of AZ31 Mg alloy

Effect of cooling rate on the microstructure and mechanical properties of ZK60 alloy

Effect of cooling rate on the microstructure and mechanical properties of sand-casting Mg-10Gd-3Y-0.5Zr magnesium alloy

Effects of Smelting and Crystallization Condition on Microstructure and Properties of AZ91D Alloy

Preferential grain growth and textural evolution of AZ31B Mg alloy during annealing after isothermal compression at 400 °C

Effective Inhibition of Anomalous Grain Coarsening in Cast AZ91 Alloys During Fast Cooling Via Nanoparticle Addition

The microstructure, fracture mechanism and their correlation with the mechanical properties of as-cast Mg-Nd-Zn-Zr alloy under the effect of cooling rate

Thermomechanical Processing and Superplasticity of AZ91 Magnesium Alloy

Grain Refinement of AZ31 Magnesium Alloy by Titanium and Low-Frequency Electromagnetic Casting

Effects of Heating Temperature on Partial Remelting Microstructure of AZ91D Magnesium Alloy

Grain Refinement Of Wrought Az61 Magnesium Alloy

The Effects of Grain Size on Ductility of AZ31 Magnesium Alloy

Effects and Mechanism of Ca on Refinement of AZ91D Alloy

Grain Refinement and Orientation of AZ31B Magnesium Alloy in Hot Flow Forming under Different Thickness Reductions

Enhancing the Mechanical Properties of Mg–Al Alloy by Introducing Al2Y Nanoparticles Via Rapid-Cooling Solidification and Optimized Heat Treatments