Effect of Multi-Walled Carbon Nanotubes on the Properties of Polyoxymethylene

Sun Yao,Bao Hada,Jia Mingyin,Guo Zhaoxia,Yu Jian

DOI: https://doi.org/10.3724/sp.j.1105.2009.00684

2009-01-01

Abstract:Polyoxymethylene (POM)/multi-walled carbon nanotubes (MWCNT) composites were prepared by melt mixing MWCNTs and POM in a rotational rheometer. The morphology, conductive property, dynamic rheological property, thermal property and crystallization behavior of the composites were investigated. It was found that MWCNTs, without any modification, dispersed homogeneously in the POM matrix. The conductive percolation effect was observed when the MWCNTs content was 1 wt%, with the percolation threshold between 0.5 wt% similar to 1.0 wt%. The thermal conductivity of POM/MWCNT composites increased to 0.5289 W/(K m) with the addition of 1.0 wt% MWCNTs, 1.5 times higher than that of pure POM [0.198 W/(K m)]. When the content of MWCNTs is further increased, the thermal conductivity of the composites hardly changed. The effective media approach (EMA) was used to confirm that the moderate increase of thermal conductivity was contributed to the interfacial resistance between MWCNTs and POM. MWCNTs have significant nucleating effect on POM, and 0.5 wt% MWCNTs could enhance the crystallization temperature of POM by about 6 degrees C but did not improve further with additional addition of MWCNTs. The complex viscosity, storage modulus and loss modulus of the composites increase with the content of MWCNTs.