Abstract:Diffusion bonding of additive manufactured (AM) metal parts to traditionally manufactured metal parts could simultaneously achieve large-scale, complex-structure, and multi-material parts. However, there is a lack of study on diffusion bonding as well as its interface formation mechanism between AM metal parts and traditionally manufactured metal parts. In this study, diffusion bonding was performed to join AM 316L stainless steel and casting 45 steel at different temperatures. The element distribution, interface characteristics and shear strength of the joints were investigated, and the interface formation mechanism at different bonding temperature was analyzed in detail. The results reveal that the interface transition zone from the AM 316L steel side to the 45 steel side is composed of the metallic elements diffusion layer and the carbide layer. Moreover, an increase in bonding temperature can effectively promote interface voids closure and increase the thickness of the metallic elements diffusion layer, while the thickness of the carbide layer firstly increases and then decreases as the temperature increases. The component of the carbide layer was identified as brittle compounds (CrFe)23C6 and (CrFe)7C3. The shear strength of the joints exhibited an increasing trend with the increasing bonding temperature. Interestingly, a sudden decrease in strength was found at 950 °C due to the significant increase of the brittle carbide layer, while high-quality joints could be achieved as the brittle carbides dissolve at 1000 °C. This study could lay the foundation for understanding diffusion bonding interface behaviors between AM metal parts and traditional casting metal parts.

Superplasticity and Application of Superplastic Forming/Diffusion Bonding Technology

Recent development in the mechanics of superplasticity and its applications

Status of superplastic materials and research and development of new superplastic low to medium carbon alloy steel

Application of Liquid Composite Molding Technology on Aeronautics

Superplasticity and Superplastic Forming

Investigation on the Factors Influencing the Thickness Distribution of Superplastic-Formed Components

Interface Behaviors and Mechanical Properties of Diffusion Bonded 45 Steel/additive Manufactured 316L Steel Joints

The Development of High Strain Rate and Low Temperature Superplasticity in Aluminum Matrix Composites

Application of electroplastic effect in mechanical processing

Deformation mechanism and microstructure evolution during superplastic deformation of friction stir processed CoCrFeNiMn high entropy alloy

Application and exploration of friction stir welding/processing in plastics industry

Dynamic reverse phase transformation induced high-strain-rate superplasticity in low carbon low alloy steels with commercial potential

Seventy-five years of superplasticity: historic developments and new opportunities

Electroplastic Drawing and Treatment Technology and Application

Recent Development of Superplasticity in Aluminum Alloys: A Review

Metal Powder and Wire Additive Manufacturing Technology

The Prospect of Advanced Material Science and Applications

Superplastic characteristic of Mn–Si–Cr alloyed ultrahigh carbon steel realized through a novel process

Research Status and Prospect of Friction Stir Processing Technology

Research Progress of Friction Stir Additive Manufacturing Technology

Application of Plasticity Forming Technology In Automobile Manufacture Industry