Effect of Micro-plasma Treatment on Wear Behavior of 45~# Carbon Steel

Liu Gu,Wang Liuying,Hua Shaochun,Wu Yongfa

DOI: https://doi.org/10.3969/j.issn.0254-0150.2008.12.018

2008-01-01

Abstract:45# carbon steel was hardened by micro plasma transferred arc(PTA)process.Worn morphology of 45# steel was observed by scanning electron microscopy(SEM).The dry sliding wear properties of 45# carbon steel and surface hardened layer were tested and wear mechanism was discussed.The test results show that the surface hardened layer consists mainly of lath martensite and plate martensite with fine and dense structure.The microhardness of hardened layer increases from about HV200 to about HV600,and the wear volume loss is reduced from 743.44×10-11 m3 to 81.86×10-11 m3,therefore,the wear resistance of hardened layer is improved about 9 times.The wear mechanism of hardened layer is characterized as oxidation wear and abrasive wear.