Preparation of Polystyrene Nanospheres in Confined Space

Wang Xiaofeng,Yuan Qiaolong

DOI: https://doi.org/10.6023/a1112021

2012-01-01

Acta Chimica Sinica

Abstract:The poly(ethylene glycol)-b-poly(propylene glycol)-b-poly(ethylene glycol) terminated with pentacyano(4-(dimethylamino)-pyridine) ferrate (EPE-Fe) complex surfactant was synthesized and was used to be self-assembled with styrene (St) in water to form a nano-reactor (EPE-Fe-St). The free radical polymerization of styrene occurred in the confined space in nanosize. And the polystyrene nanospheres (EPE-Fe-PS) were prepared in the nano-reactor. Furthermore, ferric ion was used to cure the shell of the EPE-Fe-St to form a hardened nano-reactor (Fe-EPE-Fe-St). The styrene polymerization was also arisen in the nano-reactor to form polystyrene nanospheres (Fe-EPE-Fe-PS) with a hardened shell. The results of molecular weight and morphology of polystyrene nanospheres show that the various size of monodispersed polystyrene nanospheres in 60 similar to 200 nm have been obtained in the confined nanospace. The effect of polymerization temperature on the size of self-assembled EPE-Fe-Si is remarkable, and on the size of the Fe-EPE-Fe-St is slight. The higher molecular weight of the polystyrene has achieved more than 700000 in the confined space. In the self-assembled nano-reactor, the molecular weight of PS decreases with increase of initiator content in St solution and enhancement of polymerization temperature, and increases with augment of EPE-Fe content in water. The glass transition temperature (T-g) of the polystyrene nanospheres prepared in two kinds of the confined space are in the range of 90 similar to 137 degrees C. The T-g of polystyrene nanospheres is enhanced obviously after hardening the shell of nano-reactor whether the hardening shell arises before or after the polymerization.