Abstract:A facile and versatile method using a biopolymer as a chelating agent for silver ions and as a reducing agent for the formation of catalytic sites is proposed to prepare polystyrene (PS)/Ag core-shell microspheres. More specifically, the core-shell microspheres were fabricated by electroless plating after the formation of poly(dopamine) (PDA) on the surface of PS microspheres through insitu spontaneous oxidative polymerization of dopamine. The PS-PDA microspheres were characterized by SEM, XPS, and TGA. The results showed that a uniform PDA layer was formed on the PS microsphere surface and the thickness of the PDA layer could be well controlled by varying the concentration of dopamine solution. The PDA layer was used as a chelating agent for silver ions, as a reducing agent for the formation of catalytic sites by reducing the silver ions into silver nanoparticles, and as an adhesion layer between the PS microspheres and silver layer. SEM and XRD results indicate that the diameter of the silver nanoparticles decreased with the increase in the thickness of the PDA layer. The silver nanoparticles could form a continuous and compact silver layer on the surface of the PS microspheres. Furthermore, the PS-PDA/Ag core-shell microspheres showed a good conductivity of 10S/cm and a low effective density of 1.8 g/cm(3), much lower than the corresponding values for block silver. Finally, hollow silver microspheres could be prepared by removing the PS core through calcination. SEM images showed that the hollow Ag microspheres remained unbroken and retained the spherical shape.

Preparation of Polystyrene-Encapsulated Silver Hollow Spheres Via Self-Assembly of Latex Particles at the Emulsion Droplet Interface

Preparation of monodisperse polystyrene particles and assembly of spherical colloidal crystals

A Facile Method to Synthesize PS/Ag Composite Micro-spheres

Colloidal silver deposition onto functionalized polystyrene microspheres

Facile method to prepare monodispersed Ag/polystyrene composite microspheres and their properties

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Facile Method to Synthesise Polystyrene/silver Composite Nanoparticles with Core–shell Structures

Preparation and Characterization of Polystyrene/ag Core–shell Microspheres – A Bio-Inspired Poly(dopamine) Approach

Preparation of Silver-Coated Polystyrene Composite Particles

Facile Fabrication Method And Characterization Of Hollow Ag/Sio2 Double-Shelled Spheres

A Facile Method for Preparation of Monodispersed Au/Polystyrene Composite Microspheres and Investigation on Their Properties

Fabrication and Characterization of Ag@PS Composite Nanospheres

Facile Preparation of Ordered Arrays of Polystyrene Spheres Dissymmetrically Decorated with Gold Nanoparticles at Air/liquid Interface and Their SERS Properties

Spherical Polyelectrolyte Brushes as Templates to Prepare Hollow Silica Spheres Encapsulating Metal Nanoparticles

Fabrication of compact silver nanoshells on polystyrene spheres through electrostatic attractionElectronic supplementary information (ESI) available: Preparation and characterization of PS spheres. Fig. S1: SEM micrographs of silver–latex composites. See http://www.rsc.org/suppdata/cc/b1/b110164c/

Synthesis of Silver Nanoparticle-Coated Poly(styrene-Co-sulfonic Acid) Hybrid Materials and Their Application in Surface-Enhanced Raman Scattering (SERS) Tags

A Facile Method for the Synthesis of Zns/Polystyrene Composite Particles and Zns Hollow Micro-Spheres

A Solvent-Assisted Route for Coating Polystyrene Colloids with Ag and the Corresponding Hollow Ag Spheres

Investigation of heterogeneous nucleation-and-growth of silver nanoparticles on polystyrene spheres

Synthesis of Ag-coated polystyrene colloids by an improved surface seeding and shell growth technique

The Preparation of Composite Microsphere with Hollow Core/Porous Shell Structure by Self-Assembling of Latex Particles at Emulsion Droplet Interface