Abstract:Tap kinds of styrene microemulsion systems were polymerized to prepare polystyrene microspheres (micro-PS), one emulsified by sodium dodecyl sulfate (SDS) and coemulsified by 1-pentanol and the other emulsified by octylphenoxypoly(ethoxyethanol) (OP-10). Micro-PS possessed an essentially atactic configuration hom H-1-NMR measurement. Comparison of LR spectra showed some conformational differences between micro-PS and ordinary atactic PS (o-PS). Each polystyrene microsphere contains only about three macromolecular chains iso-called pauci-chain microspheres!? which adopt a special conformation: individual chains are highly compact, while the whole structure of the microsphere is relatively loose in comparison with a random-coil chain in a multichain system. There were apparent differences in thermal behaviors between micro-PS and o-PS during the DSC scan. Micro-PS displayed two exotherms near 107 and 157 degrees C during the first scan. In the subsequent scan, both exotherms disappeared and only one glass transition similar to o-PS was shown. The first exotherm might be due to the sintering of polystyrene microspheres with small particle sizes. From wide-angle X-ray diffraction (WAXD) and polarizing optical microscopy (POM) studies, the second exotherm could be ascribed to the relatively compact conformation of polystyrene chains and the consequently formed slightly ordered regions inside micro-PS during the heating process. The special conformation was the driving force leading to its novel thermal behaviors. This is perhaps the first report that polystyrene from direct free radical polymerization has the ability to form some kind of ordered structure.

In-situ Emulsion Polymerization of Styrene in the Presence of Nano-Sio2

Mechanism and Process of the Redispersion of the Aggregated Nano-Sio2 Particles During Emulsion Polymerization of Styrene

STUDIES ON BULK SYNDIOTACTIC POLYMERIZATION OF STYRENE CATALYZED BY METALLOCENE

Particle morphology of syndiotactic polystyrene prepared with homogeneous metallocene catalyst

Preparation of monodisperse polystyrene particles and assembly of spherical colloidal crystals

An Improved Phase-Inversion Process for the Preparation of Silica/Poly[Styrene-Co-(Acrylic Acid)] Core-Shell Microspheres: Synthesis and Application in the Field of Polyolefin Catalysis

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Study on the Encapsulation of Silica Nanoparticles Via Dispersion Polymerization

Synthesis of SiO2/Polystyrene Nanocomposite Particles Via Miniemulsion Polymerization

Styrene mini-emulsion polymerization co-stabilized by predissolved fluoropolymer

Affecting the size of polystyrene nanoparticles by adding monomer in two stages

Synthesis of SiO<sub>2</sub>/PS composite particles via emulsion polymerization

Preparation of polymeric/inorganic nanocomposite particles in miniemulsions: II. Narrowly size-distributed polymer/SiO2 nanocomposite particles

A Novel Method for Preparing Monodispersed Polystyrene Nanoparticles

Preparation of Monodisperse and Anion‐Charged Polystyrene Microspheres Stabilized with Polymerizable Sodium Styrene Sulfonate by Dispersion Polymerization

Preparation of micron-size crosslinked microspheres by dispersion copolymerization of polystyrene/2,2′-oxy-bisethanol diacrylate

Synthesis of Organic-inorganic Hybrid Nanocapsules by Using Low Molecular Weight Droplets as Template

Monodisperse ultrafine polystyrene nanoparticles prepared by a semicontinuous microemulsion polymerization

Novel Characteristics of Polystyrene Microspheres Prepared by Microemulsion Polymerization

Controllable Preparation of Monodisperse Polystyrene Microspheres with Different Sizes by Dispersion Polymerization