Abstract:Al-Zn-Mg-Cu alloy, as an important lightweight structural material in the aerospace field, has ushered in a broader application space and proposed higher performance requirements. This paper presents the experimental investigation of the effect of Zr content on the microstructure refinement and performance improvement of cast Al-5.8Zn-2.3Mg-1.7Cu alloy, aiming to optimize the additional amount of Zr, refine the alloy grains, and improve the microstructure uniformity and mechanical properties. The chemical component, phase, and microstructure were observed by inductively coupled plasma, X-ray diffraction, optical microscope and scanning electron microscope; the hardness and mechanical properties were measured by Brinell hardness tester and tensile testing machine. The addition of different contents of Zr into the alloy can form fine dispersed or primary coarse Al3Zr phase, which has a significant effect on the microstructure and mechanical properties of the alloy. The results indicate that the addition of 0.05 wt% Zr does not significantly improve the grain refinement and mechanical properties, but the Brinell hardness reaches the maximum. As the Zr content rises, the grain refinement effect becomes more obvious, while the mechanical properties first increase and then decrease. The addition amount reaches 0.20 wt%, the second dendrite arm spacing is the smallest, the ultimate tensile strength, yield strength and elongation at room temperature reach the maximum of 296.74 MPa, 249.41 MPa and 8.26%, respectively. When the amount of Zr added exceeds 0.20 wt%, the existence of coarse and brittle primary Al3Zr phase reduces the mechanical properties, and the fracture morphology changes from ductile to brittle intergranular fracture.

Effects of Trace Cu Addition on the Microstructure and Tensile Properties of ZK60 Alloy

Effects of Cu Addition on Microstructure and Mechanical Properties of As-Cast Magnesium Alloy ZK60

Effect of Cu on Microstructure, Mechanical Properties, and Texture Evolution of ZK60 Alloy Fabricated by Hot Extrusion−shearing Process

Effects of Zr and Mg alloying on microstructure and properties of Cu-Cr-Si alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Study on the effect of enhanced magnesium and copper contents on microstructure and property of Al-Zn-Mg-Cu alloys with high zinc element content during fabrication processes

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Effect of Cu Additions on Microstructure, Mechanical Properties and Hot-Tearing Susceptibility of Mg-6Zn-0.6Zr Alloys

Effects of Mg content on microstructure and mechanical properties of low Zn-containing Al−xMg−3Zn−1Cu cast alloys

Microstructural Characteristics and Mechanical Properties of Extruded Al-4Cu-1Li-0.4Mg-0.1Zr-xZn Alloy

Microstructures and Mechanical Properties of Hot-extruded Mg-6Zn-xCu-0.6Zr(x=0,0.5,1.0,1.5) Alloys

Role of Cu on the Mechanical Properties and Microstructures Evolution of Al-xCu-1Li-0.4Mg–1Zn-0.1Zr Alloys

Influences of Mg content on the microstructures and mechanical properties of cast Al–2Li–2Cu–0.2Zr alloy

Effects of Solution Treatment on the Microstructure and Mechanical Properties of ZC61 Magnesium Alloy

Effect of composition on the microstructure and mechanical properties of Mg-Al-Zn alloys

Influence of Zr content on microstructure and mechanical properties of As-cast Al-Zn-Mg-Cu alloy

Effect of cooling rate on the microstructure and mechanical properties of ZK60 alloy

Influence of Zr Microalloying on the Microstructure and Room-/High-Temperature Mechanical Properties of an Al–Cu–Mn–Fe Alloy

Effect of Zn Addition on Microstructure and Mechanical Properties of Mg–9Gd–3Y–0.5Zr Alloy

Effects of Zn addition on microstructures and mechanical properties of as-extruded Mg-Zn-Ce-Zr alloys

Effect of Zn on Precipitation Evolution and Mechanical Properties of a High Strength Cast Al-Li-Cu Alloy