Abstract:A glassy phase containing cubic phase particles with a size of 3-5 am was formed in Cast Cu60Zr30Ti10 and Cu60Hf60Ti10 bulk alloys. The cubic phase is in a metastable state and its lattice parameter (a(0)) is 0.45 nm for the former alloy and 0.51 nm for the latter. These bulk alloys exhibit good mechanical properties of 2000-2130 MPa for tensile strength (sigma(t.f)), 2060-216OMPa for compressive strength (sigma(c.f)) and 0.008-0.017 for compressive plastic strain (epsilon(c.p)). The temperature interval of the supercooled liquid (SL) region prior to crystallization is 37 K for Cu60Zr30Ti10 and 67 K for Cu60Hf30Ti10. The primary crystallization occurred by precipitation of cubic CuZr (a(0) = 0.35 nm) in a diffusion-controlled growth mode of nuclei and an orthorhornbic Cu8Hf3 phase in an interface diffusion-control led growth of nuclei with decreasing nucleation rate. The difference in the precipitation modes is interpreted to be the origin of the difference in the SL region. Furthermore. the addition of Al to Cu-Zr and Cu-Hf alloys caused the formation of a glassy single phase in the rod form with diameters up to at least 3 mm, though bulk glassy alloy rods with critical diameters up to 1.5 mm and sigma(c.f) of 1920-2260 MPa were formed in Cu-Zr and Cu-Hf binary systems. The ternary bulk glassy alloys exhibited high sigma(c.f) of 2100-2370 MPa with epsilon(c.f) of 0.002-0.006. The addition of Pd, Pt, Ag or Au increased DeltaT(x) and a large DeltaT(x) of 102-110 K was obtained for the Cu-Hf-Al-M (M = Pd or Ag) glassy alloys. The synthesis of Cu-based bulk glassy alloys with good mechanical properties and large AT. in glassy single, and mixed glassy and cubic phase states, is important for future applications of bulk glassy alloys.

Cooling Rate, Structure, Thermal Stability and Crystallization Behaviour of Cu-Based Bulk Glass-Forming Alloys

Formation, Structure, and Crystallization Behavior of Cu-Based Bulk Glass-Forming Alloys

Glass-forming Ability, Thermal Stability of B2 CuZr Phase, and Crystallization Kinetics for Rapidly Solidified Cu–Zr–Zn Alloys

Devitrification Behavior and Glass-Forming Ability of Cu–Zr–Ag Alloys

Synthesis and Fundamental Properties of Cu-Based Bulk Glassy Alloys in Binary and Multi-component Systems

Crystallization Kinetics in Cu35ag15zr45al15 Metallic Glass

Influence of Al and Ag on the Devitrification Behavior of a Cu-Zr Glassy Alloy

Thermal Stability and Mechanical Properties of Cu-Hf-Al Base Bulk Glassy Alloys with a Large Supercooled Liquid Region of over 100 K

Glass-forming ability and differences in the crystallization behavior of ribbons and rods of Cu 36 Zr 48 Al 8 Ag 8 bulk glass-forming alloy

Glass-forming ability and differences in the crystallization behavior of ribbons and rods of Cu<sub>36</sub>Zr<sub>48</sub>Al<sub>8</sub>Ag<sub>8</sub>bulk glass-forming alloy

Microstructure and crystallization in Cu50Zr45Al5 metallic glass

Isochronal and isothermal crystallization in Zr55Cu30Ni5 Al10 bulk metallic glass

Cu-alloying Effect on Crystallization Kinetics of Ti41Zr25Be28Fe6 Bulk Metallic Glass

Thermal Stability and Mechanical Properties of Cu-Based Bulk Glassy Alloys in Cu50(Zr1-xHfx)45Al5 System

Structure and crystallization kinetics of a Cu50Zr45Ti5 glassy alloy

Cooling Rate Effects on the Microstructure and Phase Formation in Zr51Cu20.7Ni12Al16.3bulk Metallic Glass

Effect of Fe on the glass-forming ability, structure and devitrification behavior of Zr-Cu-Al bulk glass-forming alloys

Cooling rate effects on the microstructure and phase formation in Zr51Cu20.7Ni12Al16.3 bulk metallic glass

Bulk Glassy Cu-based Alloys with a Large Supercooled Liquid Region of 110 K

Thermodynamic and Kinetic Studies of the Cu–Zr–Al(–Sn) Bulk Metallic Glass-Forming System

Investigation of glass forming ability and crystallization kinetics of Zr63.5Al10.7Cu10.7Ni15.1 bulk metallic glass