Synthesis of a Cross-Linked Poly(vinyl Chloride) Microsphere by Self-Stabilized Precipitation Polymerization and Its Contribution to Superior Enhancement in Toughness and Mechanical Strength of Rigid PVC
Chuang Wang,Changtong Song,Hongyi Shu,Dongcang Sun,Liu Yang,Xianhong Zhang,Dong Chen,Yuhong Ma,Wantai Yang
DOI: https://doi.org/10.1021/acs.iecr.3c00368
2023-01-01
Industrial & Engineering Chemistry Research
Abstract:Itremains a formidable challenge to explore novel syntheticapproachesand realize a high performance for conventional plastics, especiallyfor poly(vinyl chloride). Herein, we synthesize cross-linked poly(vinylchloride) (CL-PVC) microspheres via self-stabilizedprecipitation (2SP) polymerization by using diallyl maleate (DAM)as a cross-linking agent. The effects of solvent composition, DAMconcentration, stirring rate, monomer and initiator concentration,and monomer feeding modes on the particle size, gel content (GC),and morphology of the resultant CL-PVC microspheres are evaluatedthoroughly. The mixture solvent of n-hexane and ethanolis suitable for conducting the 2SP polymerization of CL-PVC. Monodispersemicrospheres have a linear increase in diameter from 405 to 648 nmwith the DAM increasing from 0.25 to 16%. The GC values are highlyreliant on both the amount of DAM and its feeding modes. Subsequently,the CL-PVC and dioctyl phthalate-extended CL-PVC (DECL-PVC) microspheresare utilized as functional polymeric fillers in a rigid PVC resin.It is encouraging that both mechanical and impact strengths are enhancedconcurrently. When 5 phr DECL-PVC (GC = 30.08%) and DECL-PVC (GC =76.23%) are added to the rigid PVC resin, the tensile strengths thereofcan reach 73 and 78 MPa, respectively, which are much higher thanthat of the contrast (& SIM;54 MPa). Meanwhile, the highest impactstrength can reach 4.36 kJ/m(2) by using 5 phr DECL-PVC (GC= 30.08%) as a toughening modifier, which increased by 53.0% thanthat of CL-PVC (2.85 kJ/m(2)) at a similar loading contentand 209.2% than that of pure PVC (1.41 kJ/m(2)). This workoffers a novel strategy for the synthesis of the CL-PVC microsphereand opens a new scope for its further use.