Abstract:In this paper, porous zinc oxide (ZnO) nanosheets were successfully prepared by a simple low-temperature hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) tests showed that the synthesized product was ZnO with porous sheet structure. The diameter of porous nanosheets was about 100 nm and the thickness was about 8 nm. As a photocatalyst, the degradation efficiencies of porous ZnO nanosheets for methyl orange (MO), methylene blue (MB) and Rhodamine B (RhB) were 97.5%, 99% and 96.8%, respectively. In addition, the degradation efficiency of ZnO for mixed dyes (Mo, MB and RhB) was satisfactory, reaching 97.7%. The photocatalytic stability of MB was further tested and remained at 99% after 20 cycles. In the experiment, ZnO/FTO (fluorine-doped tin oxide) composites were prepared by using ZnO as the conductive layer. Titanium dioxide (TiO2) was deposited on the surface of ZnO/FTO by electrodeposition, so as to obtain a TiO2/ZnO/FTO composite. By studying the electrochromic properties of this composite, it was found that the TiO2/ZnO/FTO composite shows a large light modulation range (55% at 1000 nm) and excellent cycle stability (96.6% at 200 cycles). The main reason for the excellent electrochromic properties may be the synergistic effect between the porous structure and the polymetallic oxides. This study is helpful to improve the photocatalytic efficiency and cycling stability of metal oxides, improve the transmittance of thin films and provide a new strategy for the preparation of ZnO composite materials with excellent photocatalytic and electrochromic properties.

Synthesis and Cathodoluminescence Properties of Porous Wood (Fir)-Templated Zinc Oxide

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Enhanced Visible Light Response of ZnO Porous Thin Film by Post-Annealing Treatment

Facile Fabrication of Porous ZnO by a Template Free Method

Effect of Solution Concentrations on Crystal Structure, Surface Topographies and Photoluminescence Properties of ZnO Thin Films

Preparation of ZnO Particle with Novel Nut-Like Morphology by Ultrasonic Pretreatment and Its Luminescence Property

Synthesis and Hierarchical Pore Structure of Biomorphic Manganese Oxide Derived from Woods

Structural and Optical Properties of Porous ZnO Nanorods Synthesized by a Simple Two-Step Method

Synthesis of Snowflake-Like Multi-Layered Zno with Controllable Pore Sizes and Its Photocatalytic Property

Fabrication of Porous Cubic Architecture of ZnO Using Zn-terephthalate MOFs with Characteristic Microstructures.

Synchrotron Radiation XAFS Investigation on Wood Structure Hierarchical Porous ZnO

Disordered ZnO nanoparticles with extremely intense deep-level emission and enhanced photocatalytic activity

Synthesis of the Porous ZnO Nanosheets and TiO2/ZnO/FTO Composite Films by a Low-Temperature Hydrothermal Method and Their Applications in Photocatalysis and Electrochromism

Hierarchically Porous ZnO with High Sensitivity and Selectivity to H2S Derived from Biotemplates

Synthesis of porous ZnO micro-flakes via an integrated autoclave and pyrolysis process

Preparation and optoelectronic properties of hierarchical porous zno microspheres

Generalized Preparation of Porous Nanocrystalline Znfe2o4 Superstructures from Zinc Ferrioxalate Precursor and Its Superparamagnetic Property

Defect-Related Photoluminescence and Photocatalytic Properties of Porous Zno Nanosheets

A Template-Free CVD Route to Synthesize Hierarchical Porous ZnO Films

Microstructure and Infrared Absorption of Biomorphic Chromium Oxides Templated by Wood Tissues

The synthesis of hierarchical porous iron oxide with wood templates