Abstract:Mesoporous ZnO microspheres with a diameter of about 10 mu m were prepared through the combination of a membrane-dispersion microstructured reactor with a hydrothermal process. First, ZnSO4 reacted with NH4HCO3 in a membrane-dispersion reactor to produce the Zn-5(CO3)(2)(OH)(6) precursor, and then the precursor was treated at the temperature of 80 degrees C for 2 h to form the Zn-5(CO3)(2)(OH)(6) microspheres aided by the surfactant CTAB or F127; after the calcinations, mesoporous ZnO microspheres were obtained. The experimental results showed that the morphology of ZnO microspheres obtained using the membrane-dispersion microstructured reactor to mix the raw materials was better than that of those obtained using stirred tanks. Without surfactants and the hydrothermal treatment of the precursors, uniform ZnO microspheres could not be obtained. The SEM images showed that the monodispersed ZnO microspheres were assembled by the plates, and deeper observations revealed that these plates were aggregated by the ZnO nanorods formed by ZnO nanoparticles with a diameter of 9.0 nm. The adsorption-desorption isotherm curve indicated that the ZnO microspheres had mesoporous structures with an average pore diameter of 13.8 nm when using CTAB as the surfactant, and the specific surface area of the ZnO microspheres could reach 71.3 m(2)/g, much higher than that of ZnO nanoparticles.

Synthesis of porous ZnO micro-flakes via an integrated autoclave and pyrolysis process

Facile Fabrication of Porous ZnO by a Template Free Method

Synthesis of hollow ZnO microspheres by an integrated autoclave and pyrolysis process

Microwave-Assisted Rapid Synthesis Of Zno Hexagonal Quasi-Hourglasses

A Precursor-Growth-pyrolysis Approach to Two-Dimensional ZnO Micro-Platelets with Hexagonal Morphologies

Synthesis of Snowflake-Like Multi-Layered Zno with Controllable Pore Sizes and Its Photocatalytic Property

Large-Size Porous Zno Flakes with Superior Gas-Sensing Performance

Preparation and Characterization of ZnO Porous Plates

Structural and Optical Properties of Porous ZnO Nanorods Synthesized by a Simple Two-Step Method

Characteristics of ZnO Films Prepared by Ultrasonic Spray Pyrolysis Method

Fabrication of Porous Cubic Architecture of ZnO Using Zn-terephthalate MOFs with Characteristic Microstructures.

ZnO plates synthesized from the ammonium zinc nitrate hydroxide precursor

Enhanced Photocurrent and Photocatalytic Properties of Porous ZnO Thin Film by Ag Nanoparticles

Preparation of Nano-Zno Supported on Porous Carbon and the Growth Mechanism

Preparation of Mesoporous ZnO Microspheres Through a Membrane-Dispersion Microstructured Reactor and a Hydrothermal Treatment

Synthesis of octahedral ZnO mesoscale superstructures via thermal decomposing octahedral zinc hydroxide precursors

Thermal Decomposition Synthesis of Single-Crystalline Porous ZnO Nanoplates Self-Assembled by Tiny Nanocrystals and Their Pore-Dependent Magnetic Properties

Synthesis and Characterization of ZnO Ellipsoid-like Nanostructures

Preparation and optoelectronic properties of hierarchical porous zno microspheres

Novel ZnO microballs synthesized via pyrolysis of zinc-acetate in oxygen atmosphere

Synthesis and Cathodoluminescence Properties of Porous Wood (Fir)-Templated Zinc Oxide