Abstract:Uniform CeO(2) nanoflowers were synthesized by rapid thermolysis of (NH(4))(2)Ce(NO(3))(6) in oleic acid (OA)/oleylamine (OM), by a unique 3D oriented-attachment mechanism. CeO(2) nanoflowers with controlled shape (cubic, four-petaled, and starlike) and tunable size (10-40 nm) were obtained by adjusting the reaction conditions including solvent composition, precursor concentration, reaction temperature, and reaction time. The nanoflower growth mechanism was investigated by in situ electrical conductance measurements, transmission electron microscopy, and UV/Vis spectroscopy. The CeO(2) nanoflowers are likely formed in two major steps, that is, initial formation of ceria cluster particles capped with various ligands (e.g., OA, OM, and NO(3) (-)) via hydrolysis of (NH(4))(2)Ce(NO(3))(6) at temperatures in the range 140-220 degrees C, and subsequent spontaneous organization of the primary particles into nanoflowers by 3D oriented attachment, due to a rapid decrease in surface ligand coverage caused by sudden decomposition of the precursor at temperatures above 220 degrees C in a strong redox reaction. After calcination at 400 degrees C for 4 h the 33.8 nm CeO(2) nanoflowers have a specific surface area as large as 156 m(2) g(-1) with high porosity, and they are highly active for conversion of CO to CO(2) in the low temperature range of 200-400 degrees C. The present approach has also been extended to the preparation of other transition metal oxide (CoO, NiO, and CuO(x)) nanoflowers.

CeO2 Nanorod-TiO2 Nanotube Hybrid Nanostructure: Rapid Communications of the American Ceramic Society

Synthesis and Characterization of Mesoporous Ceo2 Nanotube Arrays

Morphology-Controllable Synthesis of CeO 2 on a Pt Electrode

Growth Mechanism of Ceria Nanorods by Precipitation at Room Temperature and Morphology-Dependent Photocatalytic Performance

Deposition Of Ceo2 On Tio2 Nanorods Electrode By Dielectric Barrier Discharge Plasma To Enhance The Photoelectrochemical Performance In High Chloride Salt System

A Facile Method for Loading CeO2 Nanoparticles on Anodic TiO2 Nanotube Arrays

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

Ultrafast, Continuous and Shape-Controlled Preparation of CeO2 Nanostructures: Nanorods and Nanocubes in a Microfluidic System

Ceria Nanotube Formed by Sacrificed Precursors Template Through Oswald Ripening.

Synthesis of Various Metal/TiO2 Core/shell Nanorod Arrays

Formation and Oxidation State of CeO2-x Nanotubes

Hydrothermal synthesis and automotive exhaust catalytic performance of CeO2 nanotube arrays

Spontaneous Organization of Uniform CeO2 Nanoflowers by 3D Oriented Attachment in Hot Surfactant Solutions Monitored with an in Situ Electrical Conductance Technique

Photoluminescence of ZnO Nanorod-Tio2 Nanotube Hybrid Arrays Produced by Electrodeposition

Controllable synthesis, photocatalytic and electrocatalytic properties of CeO2 nanocrystals

Synthesis and characterisation of CeO2 nanoparticles and rods

Ultrasonic-Induced Synthesis of Ceo2 Nanotubes

Preparation of CeO2 nanotubes by coaxial electrospinning and its photocatalytic performance

Sonochemical Fabrication and Characterization of Ceria (CeO<sub>2</sub>) Nanowires

Shape-selective Synthesis and Oxygen Storage Behavior of Ceria Nanopolyhedra, Nanorods, and Nanocubes.

Synthesis of Fe-doped CeO2 Nanorods by a Widely Applicable Coprecipitation Route