Abstract:The porous magnetic polymer microspheres containing carboxyl group were prepared by modified suspension polymerization by using stryene (St), divinylbenzene (DVB) and methacrylic acid (MAA) as monomers in the presence of magnetic γ-Fe2O3 which was coated with oleic acid (OA). In this experiment, three modification measures were adopted. First, the surface of the magnetic particles was treated by anionic surfactant OA to improve the hydrophobicity of mciro-size magnetic γ-Fe2O 3. Second, the monomer phase containing surface modified magnetic particles and porogens was sonicated for some time to improve the dispersibility of magnetic γ-Fe2O3 in the monomer phase and strengthen absorbence of the monomer and initiator on the γ-Fe 2O3 surface. Third, the aqueous phase was added to the monomer phase, and the mixture was sonicated for some time before polymerization to make sure all the magnetic particles can be dispersed in the monomer phase to form stable and uniform droplets which is diffrent from the conventional suspension polymerization with the monomer phase added to the aqueous phase. The pretreatment and polymerization process are as follows: Firstly, 10 - 20 g sample of magnetic particles was added to 200 mL ethanol/water solution (volume ratio = 1), and sonicated in a 250 mL beaker for 0.5 h to eliminate impurities on its surface. Then, the purified magnetic powder and 120 g deionized water were mixed together in a 250 mL, three-necked flask equipped with a stirrer, a condenser and a thermometer. As the mixture heated to 85°C, the 0A (2/3 (wt/wt) to magnetic particles) was added dropwise within 15 min and the reaction was kept at pH = 5.5 for 1 h with vigorous stirring. Afterwards, the resulting materials were isolated by magnetic decantation and washed with deionized water for several times to remove the excess OA. The treated magnetic particles were dried at 50 °C for 12 h. Magnetic porous microspheres were prepared by modified suspension polymerization in a 250 mL four-neck, round-bottomed flask fitted with a mechanical stirrer, a thermometer, a reflux condenser and a nitrogen gas inlet tube. The monomer phase which consisted of 15 mL monomers (St/MAA/DVB = 9/3/3 (mL)), 0.2 g AIBN as initiator, 15 mL diluent system (toluene/n-heptane = 2/1 (V/V)) and surface treated magnetic particles was sonicated for 15min. The aqueous phase (AP) was prepared by addition of 0.48 g HEC, 0.5 g NaCl and 90 mL deionized water. Then the aqueous phase was added to the organic phase and sonicated for 15 min. Hence, the suspension system was kept at 70°C for 24 h. The polymer produced beads were filtrated and washed with hot distilled water, ethanol and acetone several times to remove water-soluble impurities, followed by soak in 1 mol/L HCl for 48 h and extraction with solvent in a Soxhlet extractor for 24 h to remove the porogens and organic impurities. The purified beads were washed with methanol and distilled water and then dried under vacuum for 24 h. FTIR, SEM, optical microscopy and TG were used to characterize the chemical composition, morphology, size and magnetic particle distribution and magnetic characteristics of magnetic polymer microsphere. FTIR analysis demonstrated that the hydrophobicity of magnetic γ-Fe2O3 was improved significantly by chemisorption and esterification after the surface modified by oleic acid. The results of FTIR and optical microscopy analysis demonstrated that the desired polymer was bonded to the surface of γ-Fe 2O3 particles, and the polymer microspheres contained carboxyl groups. But the magnetic particles were not uniformly incorporated in the magnetic microspheres because of the magnetic agglomerating force. The morphology analysis by SEM and optical microscopy confirmed that the composite magnetic γ-Fe2O3/P(St-DVB-MAA) microsphere had a good sphericity with porous structure and a relatively uniform diameter of about 0.4-0.9 mm. The results of TG analysis indicated the content of magnetite in microspheres was 12.12%.

Polymer-Grafted Magnetite Nanoparticles Via A Facile In Situ Solution Radical Polymerisation

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Preparation and Characterization of Ω-Functionalized Polystyrene–magnetite Nanocomposites

Preparation of Polymer–nanoparticle Composite Beads by a Nanoparticle-Stabilised Suspension Polymerisation

Chloromethylated Magnetic Polystyrene Composite Nanoparticles Prepared Via RAFT-mediated Surfactant-Free Emulsion Polymerization

Solvent-free Atom Transfer Radical Polymerization for the Preparation of Poly(poly(ethyleneglycol) Monomethacrylate)-Grafted Fe3O4 Nanoparticles: Synthesis, Characterization and Cellular Uptake.

Preparation of Magnetic Hybrid Nanoparticles via Surface-Initiated Polymerization from Magnetite

A novel synthetic route to metal–polymer nanocomposites by in situ suspension and bulk polymerizations

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Preparation and Characterization of Monodispersed Magnetic Nanoparticles with Carboxylic Groups Via Polymerization Induced by a Double-Bond Ended Surfactant with Acrylic Acid

Sonochemical Synthesis of Magnetite/Poly(lactic acid) Nanocomposites

In situ and post-synthesis polymer stabilization of ferromagnetic nanoparticles synthesized by a membrane or conventional reactor

Preparation and characterization of magnetic porous γ-Fe 2O3/P(St-DVB-MAA) polymer microspheres

In situ synthesis of the Ag/poly(4-vinylpyridine)-block-polystyrene composite nanoparticles by dispersion RAFT polymerization

Synthesis of PPEGMEA-g-PMAA Densely Grafted Double Hydrophilic Copolymer and Its Use As a Template for the Preparation of Size-Controlled Superparamagnetic Fe3O4/polymer Nano-Composites

Preparation of Polybenzoxazine-Functionalized Fe3O4 Nanoparticles Through in Situ Diels–Alder Polymerization for High Performance Magnetic Polybenzoxazine/fe3o4 Nanocomposites

Tailoring Emulsion Polymerization for High-Yield Synthesis of Tween 80 Stabilized Magnetic Cross-Linked Polystyrene Nanocomposite Particles

Preparation of PS Magnetic Microspheres Via Suspension Polymerization

In Situ Formation of Silica Nanoparticles Decorated with Well-Defined Homopolymers and Block Copolymers

Oleic Acid Surface Modification in the Preparation of Magnetic Nanoparticles by a Chemically Induced Transition

Two-step single-reactor synthesis of oleic acid- or undecylenic acid-stabilized magnetic nanoparticles by thermal decomposition