Abstract:In this study, a polystyrene (PS)/nano-TiO2 hybrid was prepared by a mini-emulsion polymerization process to improve the photocatalytic properties when the crosslinking agent was added. N, N'-methylenebis (acrylamide) (MbA) was used as a crosslinking agent. The effect of a crosslinking agent on the photocatalytic properties was studied. The diameter, morphology, and photocatalytic properties of the samples were characterized and discussed. The methylene blue discoloration was monitored at 660 nm by a spectrophotometer. The result showed that the L* value from the Hunter color scale for 7 wt% TiO2-PS/0.25 wt% MbA was highest at 73.73. It was noticed that the 7 wt% TiO2 - PS/0.25 wt% MbA hybrid gave the highest photocatalytic properties. The FE-SEM confirmed the well-defined structure with a spherical shape and network formation to improve the photocatalytic properties. The diameter and morphology of the PS/TiO2 hybrid were in the range of 76 nm to 95 nm by using a field emission scanning electron microscope (FE-SEM). The particle size of the 1 wt% TiO2 - PS/0.25 wt% MbA was 76 nm, which was smaller than that of the pristine PS of 88 nm. The particle size of the 7 wt% TiO2 – PS/0.25 wt% MbA hybrid was increased by 25%. The HR-TEM image of the PS/TiO2 hybrid was studied to confirm the encapsulation of TiO2 particles in the hybrid. The FFT image of PS/MbA/TiO2 7 wt% demonstrated the crystalline structure of TiO2 (dot) and the amorphous structure of PS (ring). FT-IR spectroscopy confirmed the presence of the Ti-O functional group in the PS hybrid spectra. It was noticed that the TiO2 particles were successfully encapsulated in the PS/TiO2 hybrid.

One-step preparation of PS/TiO2 nanocomposite particles via miniemulsion polymerization.

Preparation of Nanometer Tio2/Sio2 Composite Materials by Adsorption Phase Nanoreactor Technique

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Study on PS/TiO2 Nanocomposite Particles

Preparation and Characterization of Titanium Dioxide Nanoparticle/polystyrene Composites Via Radical Polymerization

One-Step Preparation of Tio2 Particles with Controllable Phase and Morphology by Plasma Electrolysis

Miniemulsion Polymerized Titania/polystyrene Core–shell Nanocomposite Particles Based on Nanotitania Powder: Morphology, Composition and Suspension Rheology

Solvent-controlled Synthesis of Three-Dimensional TiO2 Nanostructures Via a One-Step Solvothermal Route

A One-Step Method to Prepare Monodisperse Polymer Particles in the Micron Size Range

Fabrication and Characterization of Raspberry-Like Pst/Sio2 Composite Microspheres Via Miniemulsion Polymerization

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Synthesis of Raspberry-Like Sio2/Polystyrene Nanocomposite Particles Via Miniemulsion Polymerization

Synthesis of TiO2–SiO2/polymer Core–shell Microspheres with a Microphase‐inversion Method

Synthesis of Raspberry‐like Silica/polystyrene/silica Multilayer Hybrid Particles Via Miniemulsion Polymerization

One‐step Synthesis of Ag@PS Nanospheres Via Flash Nanoprecipitation

Synthesis of SiO2/Polystyrene Nanocomposite Particles Via Miniemulsion Polymerization

One-step Hydrothermal Synthesis of a TiO2-Ti3C2Tx Nanocomposite with Small Sized TiO2 Nanoparticles

Photocatalytic Surface-Initiated Polymerization on TiO2 Toward Well-Defined Composite Nanostructures

One-step facile synthesis of monodisperse raspberry-like P(S-MPS-AA) colloidal particles

Fabrication of PS-TiO2 hybrid via mini-emulsion polymerization: Study the effect of crosslink on the photocatalytic properties of the hybrid

Preparation of Monodisperse Polystyrene Particles from Emulsifier-Free Miniemulsion Polymerization