Abstract:In this paper, the problem of crack initiation and propagation under compression shear load is investigated experimentally. The influence of far-field compression stress perpendicular to the crack surface on the initiation and propagation of the crack in brittle material is emphasizeded. With the help of the two-axis loading test machine, the two shaft displacements and forces can be adjusted freely during loading. Thus a kind of single-edge symmetric double-crack compression-shear specimen is designed. During the loading, the compression stress stoped as it reaches a series of preset values, while the shear stress increases monotonically till to the crack initiation and propagation. Then the crack initiation and propagation law of compression shear crack under different preset compression stresses can be obtained. It can be find from the test that as the compression stresses relatively smaller, along with the preset compression stress increases, the crack initiation angle increases and the deviation of crack propagation path from the initial crack direction changes severely. As the compression stress reached a definated value, the initiation angle is not changed. It can be find from the test sample that the two crack surfaces are contacted after this definated value of compression stress. The results show that the effect of compression stress on the crack propagation can be divided into two stages according to whether the crack surface contacted or not. Before the crack closed, the influence of compression stress on crack initiation load, crack initiation angle and propagation path increases,when the preset compression stress increases the crack initiation load and the crack initiation angle increase, and the propagation path deviates from the initial crack direction severely. After the crack closed, although the compression stress increases, the crack initiation angle and the critical compression shear stress ratio are keep unchanged. In addition, there existes a certain correspondence between the crack initiation angle and the compression-shear stress ratio at the time of crack initiation. When the ratio of compression-shear stress at the crack initiation increases, the crack initiation angle increases, and vice versa.

Influence of Stress Parallel to Crack Plan on Subcritical Crack Propagation in Glass under Biaxial Stress

Comparative Study on Crack Initiation and Propagation of Glass under Thermal Loading

Static Shear Fracture Influenced by Historic Stresses Path and Crack Geometries in Brittle Solids

Phase-field-crystal Simulation of Nano-Single Crystal Microcrack Propagation under Different Orientation Angles

Effects of the transverse stress on biaxial fatigue crack growth predicted by plasticity-corrected stress intensity factor

STUDY ON THE INFLUENCE OF COMPRESSIVE STRESS ON THE COMPRESSION SHEAR CRACK PROPAGATION

033 Crack initiation and path prediction of float glass with various constrain conditions under thermal loading

Crack extension mechanism and scratch stress field model of hard and brittle materials caused by curvature effect

Study of the effect of lengths on the propagation mechanism of interconnected cracks under impact loads

Space and Time Effects of Stress on Cracking of Glass

Experimental investigation on the radial and circular crack propagation of PVB laminated glass subject to dynamic out-of-plane loading

Smeared fixed crack model for quasi-static and dynamic biaxial flexural response analysis of aluminosilicate glass plates

Development of a dynamic model for crack propagation in glazing system under thermal loading

Crack arrest and stress dependence of laser-induced surface damage in fused-silica and borosilicate glass

Investigation on Dynamic Propagation Characteristics of In-Plane Cracks in PVB Laminated Glass Plates

Numerical study on full-field stress evolution and acoustic emission characteristics of rocks containing three parallel pre-existing flaws under uniaxial compression

The effect of normal compressive stresses on the fracture behavior of mode II crack under compression and shear loads

Different Driving Mechanisms of In-Plane Cracking on Two Brittle Layers of Laminated Glass

Numerical analysis of interaction and coalescence of numerous microcracks

Study on rock crack damage and confining pressure effects on shear fracture band

An Investigation of Testing Methods on the Biaxial Mechanical Behaviors of Anisotropic Materials