Abstract:Crystal growth of barium titanate (BaTiO3) using a wet chemical reaction was investigated at various temperatures. BaTiO3 nanoparticles were obtained at an energy-efficient temperature of 80 °C. However, BaTiO3 nanocubes with a preferred size and shape could be synthesized using a solvothermal method at 200 °C via a reaction involving titanium tetraisopropoxide [(CH3)2CHO]4Ti for nucleation and fine titanium oxide (TiO2) nanoparticles for crystal growth. The BaTiO3 nanocubes showed a high degree of dispersion without the use of dispersants or surfactants. The morphology of BaTiO3 was found to depend on the reaction medium. The size of the BaTiO3 particles obtained using water as the reaction medium was the largest among the particles synthesized using various reaction media. In the case of alcohol reaction media, the BaTiO3 particle size increased in the order methanol, ethanol, 1-propanol, 1-butanol, and 1-pentanol. Furthermore, BaTiO3 powder obtained using alcohol reaction media resulted in cubic shapes as opposed to the round shapes obtained when water was used as the medium. We found that the optimal condition for the synthesis of BaTiO3 nanocubes involved the use of 1-butanol as the reaction medium, resulting in an average particle size of 52 nm, which is the average distance of the cubes measured diagonally from corner to corner, and gives an average side length of 37 nm, and a tetragonal crystal system as evidenced by the powder X-ray diffraction pattern obtained using high-energy synchrotron X-rays. The origin of the spontaneous polarization of the BaTiO3 tetragonal crystal structure was clarified by a pair distribution function analysis. In addition, surface reconstruction of BaTiO3 nanocubes led to an outermost surface comprising two layers of Ti columns.

Controlling the Size of BaF2 Nanocubes from 1000 to 10 Nm

Nucleation and Growth of BaFxCl2−x Nanorods

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Stabilization of Size-Controlled BaTiO3 Nanocubes via Precise Solvothermal Crystal Growth and Their Anomalous Surface Compositional Reconstruction

Morphology and diameter controllable synthesis of boron nanowires

Shape control of CdSe nanocrystals

A general and facile strategy for precisely controlling the crystal size of monodispersed metal-organic frameworks via separating the nucleation and growth.

Shape- and Size-controlled Growth of ZnS Nanostructures

Size-Controllable Luminescent Single Crystal CaF2 Nanocubes.

Monodisperse BaF2 Nanocrystals: Phases, Size Transitions, and Self‐Assembly

Controlled Growth along Circumferential Edge and Upconverting Luminescence of Β-Nayf4: 20%yb3+, 1%er3+ Microcrystals

Size-Controllable Growth of Single Crystal In(OH)3 and In2O3 Nanocubes

Tetragonality and size control of barium titanate nanopowders prepared by solvothermal method

Sonochemical Syntheses Of Baf2 Nanoparticles And Cubes

Deep insights into the growth pattern of palladium nanocubes with controllable sizes

Size-controlled Synthesis of BiFeO 3 Nanoparticles by a Facile and Stable Sol–gel Method

Seed-Mediated Synthesis Of Ag Nanocubes With Controllable Edge Lengths In The Range Of 30-200 Nm And Comparison Of Their Optical Properties

The Combination of Colloid-Controlled Heterogeneous Nucleation and Polymer-Controlled Crystallization: Facile Synthesis of Separated, Uniform High-Aspect-Ratio Single-Crystalline BaCrO4 Nanofibers

Nucleation and Growth of CeF3 and NaCeF4 Nanocrystals

Size-controllable luminescent single crystal CaF2 nanocubesElectronic supplementary information (ESI) available: two TEM images and two PL spectra. See http://www.rsc.org/suppdata/cc/b3/b303614f/