Abstract:In this study, Eu3+-doped nanocrystalline Ca10(PO4)6(OH)2 (Ca10−xEux(PO4)6(OH)2) with different particle sizes have been prepared by the thermal decomposition of precursors. Size-dependent microstructure could be observed in nanocrystalline Ca10−xEux(PO4)6(OH)2. The lattices of Ca10−xEux(PO4)6(OH)2 nanocrystals were more distorted in comparison with the bulk, and the smaller the particle size, the more distorted the lattices. Room temperature photoluminescence showed europium site preference was also size-dependent, with the majority of Eu3+ ions occupying Ca(II) sites in the bulk, but more and more Eu3+ ions occupying Ca(I) sites in Ca10−xEux(PO4)6(OH)2 with decreasing particle size. Fluorescent properties of Ca10−xEux(PO4)6(OH)2 were considered to be influenced by both microstructure and site preference of Eu3+ ions. An abnormal strong intensity of 5D0–7F0 transition was observed in bulk and larger Ca10−xEux(PO4)6(OH)2 nanocrystals, but the relative intensities of 5D0–7F0 transition to 5D0–7F1,2,3,4 transition of Eu3+ became weaker as the particle sizes decreased. As the particle sizes became smaller, the ratios of the red emission transition (5D0–7F2) to the orange emission transition (5D0–7F1) (R/O values) first increased by comparing the bulk sample with 96nm sample, and then decreased by comparing 96nm sample to 57nm sample. The quenching concentrations of Ca10−xEux(PO4)6(OH)2 samples increased with decreasing particle size. Possible mechanisms responsible for these phenomena were proposed. Since nanosized Ca10−xEux(PO4)6(OH)2 showed higher fluorescent intensities, higher R/O values and higher quenching concentrations, this material is considered to be a promising phosphor.

Size-controllable luminescent single crystal CaF2 nanocubesElectronic supplementary information (ESI) available: two TEM images and two PL spectra. See http://www.rsc.org/suppdata/cc/b3/b303614f/

Size-Controllable Luminescent Single Crystal CaF2 Nanocubes.

Controllable Growth of Ce3+-doped Fluoride Nanocrystals (laf3/klaf4) in Fluorosilicate Glass

Synthesis and Luminescence Behavior of Eu3+-doped CaF2 Nanoparticles

Size- and Concentration-Dependent Eu2+/Eu3+ Mixed Luminescent Characteristics of Rare-Earth-doped CaF2 Nanoparticles and Their Monolithic Epoxy Nanocomposites

Size-dependent Luminescence of Nd3+-doped LiYF4 Nanocrystals

Elaboration, Structure and Luminescence of Sphere-Like CaF2:RE Sub-Microparticles by Ionic Liquids Based Hydrothermal Process

Controlled Synthesis and Up-Conversion Emission of Rare-Earth Tri-Doped NaYF4 Nanocrystals under Femtosecond-Laser Excitation.

Hydrothermal Synthesis and Luminescent Properties of CexGd1−xF3:Ln3+nanocrystals

Synthesis and Luminescence Characteristics of Nitride Ca1.4al2.8si9.2n16:Ce3+, Li+ for Light-Emitting Devices and Field Emission Displays

Doping-Mediated Size and Structure Tailoring of CaS Nanocrystals

Controlled Synthesis of Luminescent Cuins2 Nanocrystals and Their Optical Properties

Size-dependent microstructure and europium site preference influence fluorescent properties of Eu3+-doped Ca10(PO4)6(OH)2 nanocrystal

Monodispersed LaF3 nanocrystals: shape-controllable synthesis, excitation-power-dependent multi-color tuning and intense near-infrared upconversion emission

Lanthanide-doped Na(x)ScF(3+x) nanocrystals: crystal structure evolution and multicolor tuning.

Solvothermal Synthesis and Luminescence Properties of BaCeF5, and BaCeF5:Tb3+ Nanocrystals

Controlling the Size of BaF2 Nanocubes from 1000 to 10 Nm

Phase-tunable Synthesis and Upconversion Photoluminescence of Rare-Earth-doped Sodium Scandium Fluoride Nanocrystals

Upconversion Luminescence of Monodisperse Caf2:Yb3+/Er3+ Nanocrystals

Improved Multiphoton Ultraviolet Upconversion Photoluminescence In Ultrasmall Core-Shell Nanocrystals

Synthesis and Tunable Photoluminescence of NaYF4:Eu/Ba Nanocrystals