The synthesis of mesoporous aluminosilicate using microcline for adsorption of mercury(II).

Xiu-Wen Wu,Hong-Wen Ma,Jin-Hong Li,Jun Zhang,Zhi-Hong Li

DOI: https://doi.org/10.1016/j.jcis.2007.06.074

IF: 9.9

2007-01-01

Journal of Colloid and Interface Science

Abstract:An economical mesoporous aluminosilicate was synthesized with microcline as starting material and the precursor 13X zeolite as seed for crystal structure on mesoporous walls. In this method, a mixture of microcline and Na2CO3 with a molar ratio of 1:1.05 was first calcined at 1093 K for 2.5 h. The calcined materials were mixed with 35 ml C16TMABr aqueous solution (containing 8.2 g C16TMABr) and the precursors of 13X zeolite, resulting in mesoporous aluminosilicate after crystallization of the solution at 378 K for 48 h and calcination of the powder at 823 K for 5 h. The as-synthesized sample has a uniform pore diameter distribution centered at 3.7 nm. The as-synthesized sample had BET surface area of 725 m2/g and BJH mean pore diameter of 3.7 nm. The FT-IR results revealed that the building units of 13X zeolite were inserted into the pore walls of the as-synthesized sample. The adsorption ratio of mercury(II) onto the as-synthesized adsorbent was about 95%. The adsorption process was found to be spontaneous and can be explained by particle diffusion and chemical ion-exchange mechanisms. The equilibrium concentration of mercury(II) using the as-synthesized sample as the adsorbent was under 1 microg/L, making the concentration of mercury meet the limit for drinking water in China as recommended by the World Health Organization.