To Eliminate the Composition Transient Zone in Directional Solidification of TiAl Alloys

C. J. Zhang,D. M. Xu,H. Z. Fu,W. S. Bi,Y. Q. Su,J. J. Guo

DOI: https://doi.org/10.1016/j.jcrysgro.2008.04.054

IF: 1.8

2008-01-01

Journal of Crystal Growth

Abstract:The technique of directional solidification (DS) with cold-crucible and seeding is used to control the lamellar orientations in the solidified structures of TiAl alloys. However, the concentration transient zone (CTZ), a characteristic of alloy DS, may result in failure of the structure control because the CTZ separates the seed and the directionally solidified peritectic structure of TiAl alloys due to the β-phase formation. A composition adjusting method is proposed to eliminate the CTZ in this paper. Measurements were carried out to determine the macro-composition distributions in the directionally solidified Ti–Al%–Si% samples with and without the composition adjustment. The CTZ length measured in the directionally solidified sample without composition adjustment shows to be comparable to that predicted by a zone-melting-equivalent modeling performed in the present work. The experimental results for the CTZ control in zone-melting-like DS process with a cold crucible are exhibited. These results show that the CTZ control is feasible.