Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

State of Doped Phosphorus and Its Influence on the Physicochemical and Photocatalytic Properties of P-Doped Titania

Effect of the P/Ti Ratio on the Visible-Light Photocatalytic Activity of P-Doped Tio2

Effect of Calcined Atmosphere on the Photocatalytic Activity of P-doped TiO2

Photocatalytic properties of phosphor-doped titania nanoparticles

P-doped TiO_2 Immobilized Diatomite and Its Photocatalytic Performance under Visible Light

Visible-Light-Driven Titania/Silica Photocatalyst Co-Doped with Boron and Ferrum

Hydrothermal Synthesis and Characterization of Phosphorous-Doped Tio2 with High Photocatalytic Activity for Methylene Blue Degradation

Novel Thermally Stable Phosphorus-Doped TiO2 Photocatalyst Synthesized by Hydrolysis of TiCl4

Visible-light-driven Boron/ferrum/cerium/titania Photocatalyst

Synthesis and Characterization of Phosphor and Nitrogen Co-Doped Titania

Phosphor-Doped Titania - A Novel Photocatalyst Active in Visible Light

Role of Phosphorus in Synthesis of Phosphated Mesoporous TiO2 Photocatalytic Materials by EISA Method

Impurity Concentration Dependence of Optical Absorption for Phosphorus-Doped Anatase TiO2

Phosphorus-doped TiO2 for visible light-driven oxidative coupling of benzyl amines and photodegradation of phenol

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Engineering high-efficient phosphorus-doped TiO 2 photocatalyst employed for a sophisticated visible-light driven photocatalytic coating

Photocatalytic Performance Study of Organophosphorus-Doped Tungsten Trioxide and Composite Materials

Study the High Photocatalytic Activity of Vanadium and Phosphorus Co-Doped TiO2 from Experiment and DFT Calculations

Role of carbon in titania as visible-light photocatalyst prepared by flat-flame chemical vapor condensation method

Photodegradation of an Azo Dye Using Immobilized Nanoparticles of TiO2 Supported by Natural Porous Mineral.

The Chemical States and Properties of Doped TiO2 Film Photocatalyst Prepared Using the Sol–Gel Method with TiCl4 As a Precursor