Abstract:P-doped TiO2 nanoparticles were synthesized by the sol-gel method with various H3PO4 amounts. The samples were calcinated at different temperature and charactered by XPS, ICP, XRD, SEM, Raman, FTIR, and UV-vis methods, so that the formation process of phosphate species could be inspected. The XRD results show that P species hinder the particle growth of anatase and increase the anatase-to-rutile phase transformation temperature to more than 900 degrees C, and a new titanyl phosphate, Ti5O4(PO4)(4), was observed in P-doped TiO2 when calcined at 1000 degrees C. The UV-vis results indicate that the P species is likely to have two different states, leading to the variety of visible-light photocatalytic activity and band gap energy of P-doped TiO2. One state is the "separated phase". In this state, the P/Ti ratio is very low so that the P species is surrounded by TiO2. The "separated phase" of P species introduces oxygen into TiO2 lattice and hence causes a red-shift of the adsorption band edge of anatase, leading to the increased visible-light photocatalytic activity of P-doped TiO2. The other state is the "congregated phase". It appears at the micro region where the ratio of P/Ti is high enough to make the TiO2 clusters isolated by P species. The "congregated phase" of P species acts as the interface phase between TiO2 clusters and strongly retards the crystal growth of anatase, resulting in the widened band gap of P-doped TiO2. Furthermore, a possible mechanism was also proposed to explain the formation of the two phases during the sol-gel process. The results indicate that in order to improve the visible-light photocatalytic activity of P-doped TiO2 the percentage of "separated phase" in P species needs to be enhanced.

Phosphor-Doped Titania - A Novel Photocatalyst Active in Visible Light

Photocatalytic properties of phosphor-doped titania nanoparticles

Yellow–colored Mesoporous Pure Titania and Its High Stability in Visible Light Photocatalysis

Visible-light-driven Boron/ferrum/cerium/titania Photocatalyst

Visible-Light-Driven Titania/Silica Photocatalyst Co-Doped with Boron and Ferrum

Soft-chemical Synthesis of Mesoporous Nitrogen-Modified Titania with Superior Photocatalytic Performance under Visible Light Irradiation

State of Doped Phosphorus and Its Influence on the Physicochemical and Photocatalytic Properties of P-Doped Titania

Synthesis and Characterization of Phosphor and Nitrogen Co-Doped Titania

Synthesis of Phosphorus-Doped Titania with Mesoporous Structure and Excellent Photocatalytic Activity

Novel Thermally Stable Phosphorus-Doped TiO2 Photocatalyst Synthesized by Hydrolysis of TiCl4

Phosphorus-doped TiO2 for visible light-driven oxidative coupling of benzyl amines and photodegradation of phenol

Visible-Light-Activated Nanoparticle Photocatalyst of Iodine-Doped Titanium Dioxide

P-doped TiO_2 Immobilized Diatomite and Its Photocatalytic Performance under Visible Light

Role of carbon in titania as visible-light photocatalyst prepared by flat-flame chemical vapor condensation method

Effect of the P/Ti Ratio on the Visible-Light Photocatalytic Activity of P-Doped Tio2

Preparation and Photocatalytic Activity of Yellow Titania

Hydrothermal Synthesis and Characterization of Phosphorous-Doped Tio2 with High Photocatalytic Activity for Methylene Blue Degradation

Recent Progress In Titania Photocatalyst Operating Under Visible Light

Preparation of Phthalocyanine-Modified Mesoporous Titania and Its Visible-Light Photocatalytic Activity

Synthesis and Characterization of Nitrogen and Phosphate Codoped Titanium Dioxide with Excellent Visible–light Photocatalytic Activity

Simple Fabrication of Twist-Like Helix N,S-codoped Titania Photocatalyst with Visible-Light Response