Abstract:The primary goal of this study is to examine the impact of sodium hydroxide (NaOH)/alkali-activated fly ash on the fresh properties and mechanical properties of self-compacting concrete (SCC). The fresh properties, known as the workability of SCC characteristics, were determined using the U-box, V-funnel, J-ring, and L-box tests. The M30 grade SCC containing superplasticizer of 0.86 wt. % of cement is replaced with 10%, 15%, 20%, 25%, 30%, and 40% of alkali-activated fly ash. On days 7, 14, and 28 after curing, the compressive strength and the splitting tensile strength of the SCC were examined. The study was further extended to evaluate the behavior of reinforced concrete beams containing fly ash and ground granulated blast furnace slag, whose size was 1200 × 100 × 150 mm3, under flexure loading. Based on the test results, it was found that the increase in the replacement of cement with alkali-activated fly ash increased the workability in the SCC. With the addition of superplasticizers, the SCC gained much more workability than conventional concrete containing no superplasticizer. The mechanical properties of 10% and 15% activated fly ash in Portland cement provided the maximum strength for the SCC at different ages of curing. The maximum first crack load and maximum ultimate flexure loading of the reinforced concrete beam containing 10% activated fly ash by weight of cement were greater than those of the control concrete beam. The microstructural scanning electron microscope observations confirmed that the alkali-activated fly ash increased the strength properties of the self-compacting concrete.

Study on High Volume Fly Ash Concrete

Study on the Effect of Fly Ash and Polycarboxylic Acid Water Reducer on the Properties of Recycled Concrete

Study on performance of high strength pumping concrete compounded by fly ash composite powder under low water-cement ratio

Research on the High Strength Pumping Concretes with Grade-Ⅱ fly Ash and Slag Micro Powder

MECHANICAL PROPERTIES OF HIGH PERFORMANCE CONCRETE MADE WITH HIGH CALCIUM HIGH SULFATE FLY ASH

High Strength Concrete with a Large Amount of Fly Ash

Effect of Fly Ash and Activator on Performance of Steam-Cured Concrete

Study on Mechanics Property Experiments of High Fly Ash Content Concrete

Mechanical Properties of Green Structural Concrete with Ultrahigh-Volume Fly Ash

Compressive strength, flexural strength, and durability of high-volume fly ash concrete

Experimental Study on the Cracking Resistance at Early Ages of High Performance Concrete Added with Lithium Slag and Fly Ash

Effect of Fly Ash with Different Particle Size Distributions on the Properties and Microstructure of Concrete

Research on Improving Cementitious Material Properties by Adding FineFly Ash

The Influence of Fly Ash Addition on the Autogenous Shrinkage of High-Strength Concrete

Effects of ultrafine fly ash on the properties of high-strength concrete

Strength characteristics of self-compacting concrete with alkali-activated fly ash

COMPRESSIVE STRENGTH DEVELOPMENT OF COMPLEX BINDER CONTAINING FLY ASH OR QUARTZ POWDER

Optimization Of The Fabrication Technology Of Selfcompacting High Performance Concrete

lnfluence of steel slag - superfine fly ash composite mineral admixture on the properties of concrete

Study on the effect of fly ash to properties of cement admixtures

Static and Dynamic Mechanical Behavior of High Performance Steel Fiber Reinforced Concrete Mixed with High Volume Fly Ash