Abstract:To promote the innovation of raw magnesium production technology, an integrated calcination and silicothermic reduction short process for magnesium production was experimentally studied on the laboratory scale in this article. The influences of the thermal decomposition temperature, silicothermic reduction temperature, pelletizing pressures and silicon ratio on the characteristics of producing the magnesium by the short process was studied. The crosslinking effect, including reactions between CO2 decomposed from dolomite and metal elements in ferrosilicon, microstructure change at thermal decomposition and silicothermic reduction stages, was analyzed and discussed. In addition, comparison of the magnesium reduction rate and production efficiency between the new short process and the traditional Pidgeon process was made. The results indicated that the decomposition and reduction temperatures have a more significant influence on the magnesium reduction process than the pelletizing pressure and silicon ratio. A decomposition temperature < 1000 °C and reduction temperature > 1100 °C was proven to be favorable for improving the magnesium reduction rate and production efficiency of the new short process. It was also found that the integrated short process for magnesium production can reach the same total reduction rate and has lower efficiency compared to the traditional process. The decrease of magnesium production efficiency in the new short process was expected to result from reduction of the contact area and hindering of diffusion between CaO·MgO molecules and Si(Fe) atoms because of the microstructure change and ferrosilicon consumption by the reactions between CO2 and metal elements in ferrosilicon. Preparing briquettes with additives of binder or ultrafine particles of raw materials was proposed and considered for further study to improve the production efficiency.

Thermodynamic analysis and experimental study of the thermal reduction of magnesia by cokes in vacuum

Kinetics of reduction of magnesia with carbon

Kinetics and mechanism of carbothermic reduction of magnesia

Catalytic Reduction of Magnesia by Carbon

Kinetic mechanism of magnesium production by silicothermic reduction of CaO·MgO in vacuum

The effects of reductant and additive on the magnesium extraction from calcined dolomite via metallothermic reduction under vacuum condition

Mass Transfer and Reaction Kinetics in the Carbonization of Magnesium Oxide from Light Calcined Magnesia with Mechanical Force Enhancement

The Preparation of Magnesium from Magnesia by Using Atmospheric Microwave Al-C Reduction Method

Thermodynamic calculation and microstructure characterization of spinel formation in MgO–Al2O3–C refractories

Non-isothermal kinetic study of high-grade magnesite thermal decomposition and morphological evolution of MgO

Evaluating the Effect of MgO/Al2O3 Ratio on Thermal Behaviors and Structures of Blast Furnace Slag with Low Carbon Consumption

Systematic kinetic study of magnesium production using magnesium oxide and carbonic materials at different temperatures

Study of Carbonizing Processes for Sintered Dolomite

Effect of Sintering Atmosphere on Microstructures and Properties of Synthesized Microporous MgO Refractory Raw Material

Thermal decomposition of magnesium carbonate in methane atmosphere for the synthesis of syngas: The effect of O 2

Preparation of Active Magnesia with Magnesite

Experimental Study of Magnesium (Mg) Production by an Integrated Calcination and Silicothermic Reduction Short Process

Thermodynamic Analysis of the Reduction of Vanadium-titanium Magnetite by Gasification Gas

Kinetic study of the reduction reaction of red mud and CO under fluidization condition

Volatilisation behaviour of iron, silicon and magnesium during vacuum carbothermal reduction of ilmenite concentrate

Activated Sintering of Activated Carbon-Doped Magnesia