Abstract:The Aluminum Matrix Composites were manufactured by in situ reaction of Al powder, TiO2 powder, C powder. The effects of TiO2 particle size on reinforcements, reaction mode, and kinetics were studied. The results show that the reinforcements contain Al3Ti, Al2O3, TiC and AlN in Al-TiO2-C system. Al3Ti is lath-like with a length between 500–2000 μm, there is a preponderance on quantity when TiO2 particle size is 30 nm, the area account for nearly 11.5%. TiC is granular and agglomerated, granular Al2O3 mainly distribute on Al grain boundary. Also there is a small quantity of AlN, the reaction mode is solid-liquid reaction. With the increase of TiO2 particle size (200 nm), Al3Ti changed from lath to block, and the length was declined sharply to 20–60 μm. The distribution is uniform, but the area account for nearly 8.9%, compared with the Al-TiO2-C system prepared by 30 nm TiO2, the area ratio is reduced by 2.6%, the quantity is significantly decline. TiC distribution is more uniform, and the Al2O3 particles are melted and become blocky or ring what distribute on the grain boundaries or matrix of Al grains. The quantity of AlN is increased obviously, showing a ring shape, distributed on the α-Al grain boundary or phase boundary, the length is about 250 nm, and the reaction mode is solid-solid reaction. The particle size of TiO2 affects the speed of sintering process and the reaction rate. The smaller the particle size of TiO2, the faster the sintering speed. Also, at the beginning of the reaction, the smaller the particle size of TiO2, the faster the reaction rate. However, as the reaction progresses, the influence of the particle size of TiO2 is weakened.

Effect of TiC Particle Size on the Toughness Characteristics of Al2O3–TiC Composites

The Influence of TiC-particle-size on the Fracture Toughness of Al2O3–30 Wt.%tic Composites

Mechanism of toughening in TiC particulate reinforced Al2O3

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Fracture toughness of Al 2 O 3 -TiCN composites

Effect of TiC-particle Size on Sliding Wear of TiC Particulate Reinforced Alumina Composites

Influence of TiC particle size on the load-independent hardness of Al2O3–TiC composites

R-curve Behavior of TiC Particle Reinforced Al2O3 Composites

Influence of TiC particle size on microstructural evolution and fracture mechanism of TiC/Al-Cu composites

Statistical variability in the indentation toughness of TiCN particle reinforced Al2O3 composite

Investigation on Fracture Toughness of Aluminum Matrix Composites Reinforced with in Situ Titanium Diboride Particles

Processing and Characteristics of TiB 2 Toughened B-Ti-C Composites

Effect of Al content on impact resistance behavior of Al-Ti-B4C composite fabricated under air atmosphere

On the Local Crack Resistance of Al2O3–TiC Composites Evaluated by Direct Indentation Method

Effect of B4C particle size and TiB2 content on the mechanical properties of B4C composites and their dynamic mechanical properties

Preparation and toughness mechanism of in-situ Ti<sub>3</sub>AlC<sub>2</sub> enhanced and toughened TiAl<sub>3</sub> matrix composites

Effect of Particle Size on the Thermal and Mechanical Properties of Aluminum Composites Reinforced with Sic and Diamond

Preparation and toughness mechanism of in-situ Ti3AlC2 enhanced and toughened TiAl3 matrix composites

Effect of TiO(2 )particle Size on Reinforcements, Reaction Mode and Kinetics in Al-TiO2-C System

Fabrication of Al2O3–Ti3SiC2 Composites and Mechanical Properties Evaluation